1) tumbler strength index
转鼓强度指数
2) drum strength
转鼓强度
1.
The laboratory results show that the drum strength of sinters is improved,the fuel rate and productivity are increased,and RDI is decreased with the increase of Yangdi fine ore content.
随着扬地粉配入量的增加,烧结矿转鼓强度、成品率改善,燃耗有少量上升,利用系数增加,低温还原粉化指数变差。
2.
At last,the hybrid algorithm is applied to design the prediction model about relationship between the sinter composition and drum strength.
采用该方法建立炼铁过程中烧结矿成分与转鼓强度关系的预测模型,并用现场数据加以验证;实验结果表明该方法收敛速度快,所建立的模型具有较高的预测精度,可用于复杂非线性系统建模。
3.
When the above factors were considered to obtain a higher drum strength,the content of lime with three to four percent was suitable.
试验结果表明,转鼓强度随着生石灰配比的增加有增加的趋势,但当生石灰配比添加到5%时,烧结强度有明显的下降趋势。
3) tumbler index
转鼓强度
1.
The reasons of tumbler index decreasing of Shui-Steel sinter since 2007 were analyzed.
从原料结构、操作制度和设备工艺等方面分析水钢2007年以来4号、5号烧结机烧结矿转鼓强度下降的的原因,并介绍了确保烧结矿强度所采取的对策和措施。
4) tumble strength
转鼓强度
1.
Influence of additive on the sinter tumble strength;
添加剂对烧结矿转鼓强度的影响
2.
The influence of the content of CaO and SiO2(CS) on the tumble strength,and the effect of the flux of different levels on suction pressure are analyzed.
分析了烧结矿中CS值(即CaO%+SiO2%)对转鼓强度的影响,以及在不同熔剂水平下,熔剂对操作负压的影响。
3.
As a result the sinter tumble strength was increased from 69.
石家庄钢铁股份有限公司炼铁厂为改善烧结矿质量,通过优化配矿、提高料层以及烧结矿二元碱度等措施,使烧结矿转鼓强度从69 80 %提高到74 15 %,取得了显著的效果。
5) tumbler strength
转鼓强度
1.
The main reasons of sinter tumbler strength worsening in HANGZHOU Iron & Steel Co.
从原料结构变化和操作制度上分析了杭钢近半年来烧结矿转鼓强度下降的主要原因,并提出了确保烧结矿强度应该采取的措施。
2.
The results show that the finished product ratio and the productivity of the sinter have been improved after reducing MgO content,the tumbler strength of the finished product sinter ore is increased slightly,the reduction degradation index at low temperature has been improved.
分析结果表明,MgO含量降低后,烧结成品率和利用系数提高,成品烧结矿的转鼓强度略有提高,低温还原粉化指标改善。
3.
The tumbler strength of the western zone sinter is lower than others,it is unappeasable require for BF process since it is put into operate.
鞍钢西区烧结投产以来,烧结矿的转鼓强度始终较低,不能满足大高炉的生产需要,为此西部烧结作业区采取一定的措施,例如通过优化配矿,加强质量管理和提高岗位人员的操作水平,使烧结矿的强度大幅度提高,转鼓指数达到83%。
6) drum index
转鼓强度
1.
Influence of capacity expansion of sintering machine on FeO content and drum index of sinter;
烧结机扩容对烧结矿FeO含量及转鼓强度的影响
2.
On laboratorial conditions,the effect of bed permeability improvement under the condition of stand-support sintering was studied,and the productivity,drum index,product yield and size composition were investigated quantitative.
在实验的基础上,研究了烧结杯安装支撑板后对料层透气性的改善效果,进而考察了对烧结生产率、烧结矿转鼓强度、成品率、粒度组成和冶金性能等的影响。
补充资料：焦炭转鼓强度
焦炭转鼓强度
drum strength of coke
jiaolal〕zhl」allguq扭ngdu焦炭转鼓强度(drum strength of eoke)表征常温下焦炭的抗碎能力和耐磨能力的焦炭机械强度重确定生产操作条件和产品质堂管理的检测标准之要指标。作转鼓强度试验时，将焦炭置于转动的鼓内，一。借助提升板反复地提起、落下。在此过程中，焦炭与转鼓类型最初的转鼓试验装置是一个鼓面光鼓壁以及焦炭与焦炭相互撞击和摩擦，导致焦炭沿裂滑、可旋转的简单圆鼓，用以代替落下试验的多次提纹断开、表面磨损、粒度变小。焦炭强度即指焦炭经升机构。(见焦炭落下强度)试验发现，焦炭装入鼓内转鼓试验后，用大小两个粒级的焦炭量各占入鼓焦炭旋转20h、30000r后，焦炭仍未发生破裂现象。为了给量的百分率分别表示的抗碎能力和耐磨能力。转鼓强焦炭提供破碎力和磨损力，在转鼓内增加提料板、钢度是在经验基础上，通过规范性的转鼓试验方法获得棒或钢球等。表1列出了20世纪20年代以来一些国的一种块焦强度指标。转鼓强度不仅是各使用部门评家使用的转鼓转鼓大致可分为五种类型。定焦炭质量的重要依据.也是焦化厂选择炼焦用煤、(l)美、英等英制单位国家采用的转鼓(表中序 表1一些国家使用的转鼓及其主要特点一号卜只〕午径为巧了一引JmT-n.长为川‘一559mm.带(助直径大于主.srn、长度l一1.sm并带有较宽提以代，转数为I。。。一!沁or，旋转时间长达l小时提料板的封闭型转鼓(表中序号9一l飞)转数较少，仅左这一玲转鼓中焦炭经受的曦袱力比较明显美国材料有3。一50r在这种转鼓中焦炭主要受到冲击力的作和试验协全的转披试验经过多次修订已纳入ASTM用日本工业标准(JIS)为增加破坏力，增加了转鼓际准转数(3)直径1.8一2.阮1、鼓壁钻有圆孔或由钢棍组 成的转鼓(表中序号12、13、16)。焦炭在鼓内的下落 高度近似于落下试验，焦炭破损后小于一定尺寸的焦 粒可以通过鼓壁上的圆孔或钢棍间的缝隙漏出。苏联 曾将松格林转鼓列为国家标准(l’(X月，)。中国在1949 年也曾采用松格林转鼓测定块焦强度。由于这种转鼓 试样量大，设备和操作笨重，苏联和中国均已改用米 库姆转鼓测定块焦强度。 (4)直径仅500~左右、焦样量较少、转数为600 ~700r的小型转鼓(表中序号14、15)。为了增加对焦 炭的破碎力，内装有一定数量的钢球。这种转鼓类似 目前实验室内测定块焦反应后强度和结构强度(见焦 炭显徽强度)的设备，在工业上已不再使用。 (5)以德国、法国等西欧国家为主所采用的转鼓 (表中序号27~22)。直径为900一1000mm，宽度为 1000mm(或500m。)，转速为25r/min，转数为100一 50价，带提料板。