1) principal extension ratio
主拉伸比
2) draw ratio
拉伸比
1.
The stability of Nylon 66 technical yarn properties was obtained by adjusting of spinning viscosity, draw ratio, take-up tension and godet temperature.
通过调整纺丝黏度、纺丝拉伸比、卷绕张力、拉伸辊温度等可以对尼龙66工业丝物理性能的稳定起到很重要的作用,尤其是可以使其均匀性提高,三项主要物性指标工序能力控制指数(CPK)达到1级以上。
2.
The results showed that the relative molecular weight and its distribution of polypropylene, isotacticity, spinning temperature, quenching speed, draw ratio, drawing godet temperature and oiling amount had evident effect on yarn irregularity.
结果表明,聚丙烯的相对分子质量及其分布、等规度和纺丝温度、冷却吹风速度、拉伸比率、上热盘温度以及上油量等对纤维不匀率产生明显的影响。
3.
The influences of draw ratio(λ)and compatibilizer contents(C g)on PA66 fiberization and mechanical properties of the composites were investigated.
用挤出 -拉伸 -注塑法制备了PP/PA66原位复合材料 ,研究了拉伸比 (λ)和增容剂用量 (Cg)对PA66成纤性和材料力学性能的影响。
3) hot stretching ratio
热拉伸比
5) active drawing
主动拉伸
1.
The mchanism can change passive drawing to active drawing to over come some disadvantages of passive drawing,and expatiates on the theory of active drawing and compares the double forms.
介绍了一种新型薄膜预拉伸机构 ,即把被动拉伸变为主动拉伸 ,克服了被动拉伸的一些缺点 ;阐述了主动拉伸的原理作 ,并对二者进行了比
6) draft ratio
牵伸比;拉伸比
补充资料：固有拉伸比
分子式：
CAS号：
性质：也可称自然拉伸比。是指在一定温度下材料在屈服应力作用下伸长的倍数，即材料拉伸前后长度之比。各种聚合物的固有拉伸比是不同的，如聚苯乙烯为1.5～3.5，高密度聚乙烯为5～10。
CAS号：
性质：也可称自然拉伸比。是指在一定温度下材料在屈服应力作用下伸长的倍数，即材料拉伸前后长度之比。各种聚合物的固有拉伸比是不同的，如聚苯乙烯为1.5～3.5，高密度聚乙烯为5～10。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。