1) prestressed ferro-cement
预应力钢丝网水泥
2) prestressed ferrocement
顶应力钢丝网水泥
3) ferrocement
钢丝网水泥
1.
70 galvanized weldmesh ferrocement specimens were pre-deflected to the serviceability limit of 207N/mm2 stress in the outermost wire after 28 days normal curing.
使正常养护28d的70个镀锌焊接钢丝网水泥试件持续受弯，最外层钢丝的计算应力达到腐蚀状态下容许值207N／mm2，再放入自制的以70℃干燥60min和40℃3。
2.
How to effectively utilize its characters is the key step in ferrocement floating dock design.
钢丝网水泥是一种复合材料，其在船舶设计中成功应用的关键在于能否充分发挥材料的特性。
4) prestressed steel wire
预应力钢丝
1.
The demands of PCCP for prestressed steel wire are expounded emphatically from such aspects as chemical .
从化学成分、组织、钢丝的拉拔、微合金化措施等方面重点阐述PCCP对预应力钢丝的要求。
2.
The stress corrosion of cold drawn prestressed steel wire hasn't been paid full attention to for a long time.
长期以来 ,冷拉预应力钢丝的应力腐蚀问题并未引起人们的足够重视。
3.
To introduce the work principle and technical characteristics of such equipments used for producing prestressed steel wire as SG1120 reel winding machine,FX1400 reel payoff and FH1200 flower basket type payof
介绍用于预应力钢丝生产的ＳＧ１１２０工字轮打轴机、ＦＸ１４００工字轮放线机、ＦＨ１２００花篮式放线机的工作原理和技术特征。
5) PC steel wire
预应力钢丝
1.
To unite traditional drawing procedure of PC steel wire with the stabilizing treatment procedure into a non-torsion drawing continuous production line.
将传统生产预应力钢丝的拉拔工序和稳定化处理工序合并成一条无扭拉拔连续作业线,采用驱动轮直径为 1 200mm的拉丝机,减少拉拔中钢丝产生的内应力;中频感应加热去应力回火热效率高;水平施加预张力,张力轮直径 3 500mm;全线由微机控制线速度、加热温度和预张力,人机界面操作,提高生产效率、成材率和钢丝内在质量,降低原材料消耗和电能。
2.
By means of mechanical performance trials and chemical analysis,metallographical examination as well as other methods,the reasons of the brittle fracture of 5 0?mm PC steel wire are analyzed and studied It is considered that the key reasons are that the 82B raw materials have serious defects of central carbon segregation and residual shrink hol
采用力学性能试验、化学分析和金相分析等手段对 5 0mm光面预应力钢丝发生脆断的原因进行分析研究 ,认为 5 0mm光面预应力钢丝脆断的主要原因是由于 82B原料中有严重的中心碳偏析和残余缩
6) prestressed steel wires
预应力钢丝
1.
Through the test of the four prestressed steel wires at elevated temperature around the range of 20 to 800,the thermal strain of the four prestressed steel wires under stress is studied,the main reasons of the thermal strain are analyzed,and the computation equations are listed.
通过对4种常用的预应力钢丝在高温下的试验,研究了4种预应力钢丝在不同应力水平下,在20~800℃范围内的变形性能,并分析了热应变产生的主要因素,给出了相应的计算公式。
补充资料：钢丝网水泥薄壳闸门
钢丝网水泥薄壳闸门
reinforced cement shell gate
保护层厚度要严格控制在3一5毫米之间，砂浆振捣要密实，表面要排光，以提高其杭渗性。为保护钢丝网免受锈蚀，表面还要涂以防水涂料或树脂，以延长闸门的使用寿命。若养护良好，使用期可达到20年以上。薄壳门叶可视为均质弹性结构，其内力分析可按一般壳体理论进行，过去大都用近似方法手算，目前已发展为用有限元法在电子计算机上计算。翡矍豁巍豁简留蕊款霎默d。~shell gate)门叶采用薄壳结构形式，并目丝网水泥为主要建筑材料的闸门。20世纪60年代，国出现了大批以钢筋混凝土和钢丝网水泥为主要月.介J-J、11材料的闸门，形式繁多，中以钢丝网水泥薄壳闸f-为优越(见图)。由于它徽约钢材，制作简便，而f-仅与同尺寸的钢闸门大另当，故大量使用在农田寸等中小型水利工程上。 薄壳结构的形式有杖壳(折板)、球壳、圆柱隽双曲扁壳等，适用的门鲤直升式平面闸门、弧形闸‘扇型闸门和人字闸门等。丝网水泥是由钢丝网和寸砂浆组成的混合物。钢丝宜用细丝密网(一般丝径]米，网格10X10毫米)，岸层数为4一8层.必要时还嵌夹钢筋网加强。砂浆扮夕，.........叮呀﹄诊口山口一般为250一350号。由于钢丝网水泥薄壳厚度较，一般只巧一35毫米，施工要特别注意质量，钢丝网:nt用中噬其嗽布唾湘利淞湘隋工钢妮网毫翎河号卜的‘A}刊门立视图 ┌───┐ │玉 │ │T │ ┌─────────────┼───┤ │} │川 │ ├─────────────┼─┬─┼─────┬─┬───┐ │产一一-一一下厂一一一一门 │七│红│/中纵梁 │ │边柱~ │ │:知。