1) carbon mesophase microbead
碳质中间相小球体
2) carbonaceous mesophase sphere
中间相碳小球
3) mesophase sphere
中间相小球体
1.
Its mechanism is the instable mesophase sphere was formed after the pitch was heated gradually, then transforms needle cokes by coalesence.
针状焦是生产ＵＨＰ电极的重要原料，针状焦的生成机理是沥青经逐渐加温生成不稳定中间相小球体，再经堆积中间相转变为针状焦。
4) carbonaceous mesophase
碳质中间相
1.
Metallic elements Ti and Ni were doped into the coal tar pitch-derived carbonaceous mesophase(CM) through mechanical alloying in a high energy ball mill apparatus.
利用机械合金化法将金属粉Ti/Ni掺入煤焦油沥青碳质中间相中,借助X射线衍射仪分析掺入金属前后碳质中间相的结构,采用MMU-5G型高温端面摩擦磨损试验机考察不同载荷下,以掺入金属的碳质中间相为润滑油添加剂的摩擦磨损性能,用扫描电子显微镜观察磨损表面形貌,采用激光拉曼光谱仪分析磨损表面碳质材料的结构特征。
2.
A coal tar pitch-derived carbonaceous mesophase(CM) was treated in a high energy ball mill apparatus.
采用高能球磨法对煤焦油沥青碳质中间相进行了非平衡处理,利用X射线衍射和激光Raman光谱技术研究了中间相高能球磨前后的结构变化,并且使用SRV高温摩擦磨损试验机考察了碳质中间相的摩擦性能。
3.
Incorporation of metallic element Ni into the coal tar pitch-derived carbonaceous mesophase(CM) was performed through mechanical alloying in a high energy ball mill apparatus.
采用机械合金化法在煤焦油沥青碳质中间相中掺杂元素镍,借助X射线衍射仪和激光Ram an光谱仪研究了掺杂元素前后中间相的结构变化,利用SRV高温摩擦磨损试验机考察了机械合金化法掺杂元素镍的碳质中间相作为润滑油添加剂的高温摩擦磨损性能。
5) mesophase microbead
中间相小球
6) meso-sphere
中间相小球体沥青
补充资料：中间相
合金相图中在中间成分区域内形成的均质相。晶体结构一般和组元金属不同,物理、化学和力学性质也迥异。中间相是一类重要的合金相。按照结合键的类型，中间相可以分为离子化合物、共价化合物和金属化合物；按照它们的形成规律和结构、性能特征,又可区分为正常价化合物、电子化合物、 间隙化合物和拓扑密堆相（TCP相）。这些化合物一般具有金属性质,只一部分正常价化合物例外。习惯上中间相又常被称为金属间化合物(in-termetallic compound)。但也有人把成分范围较宽的中间相区分为Ⅱ类固溶体(secondary solid solution)，而用金属间化合物一词专指均质范围比较狭窄，化学计量比较简单的中间相（见合金相）。