1) calcium aluminate chloride hydrate,calcium chloroaluminate hydrate
水化氯铝酸钙
2) cementitious property
水化铝酸钙
1.
The study of hydration products, hydration process and hardened pastes results that anhydrous has cementitious property, longer setting time, higher late strength and obvious expansion in the presence of gypsum.
用分析纯原料合成了水化铝酸钙纯样品，用ＤＴＡ－ＴＧ、ＸＲＤ研究了脱水过程及脱水相组成和特性；用ＸＲＤ定量分析了脱水相水化产物和水化速度；考察了脱水相的凝结时间与硬化体强度，本文为建立４００℃左右低温脱水的水化物脱水相（ＤｅｈｙｄｒａｔｅｄＨｙｄｒａｔｅｓＰｈａｓｅｓ简称ＤＨＰ）胶凝材料新体系提供了理论依据。
3) calcium chloroaluminate
氯铝酸钙
4) aluminum calcium chloride
氯化铝钙
1.
Study on the treatment of the scrubbing water of blast furnace by aluminum calcium chloride;
用氯化铝钙处理高炉煤气洗涤水实验研究
2.
A new kind of flocculant - aluminum calcium chloride is prepared by baking technic to synthesize pure calcium aluminate.
通过采用焙烧工艺合成高纯铝酸钙,制备高效氯化铝钙混凝剂的方法,研制一种生产高效絮凝剂的新工艺技术;对焙烧和酸溶工艺在制备过程中的作用进行了探讨;应用该混凝剂对本钢转炉集尘洗涤水进行了处理试验。
5) calcium aluminates hydrate C3AH6
水化铝酸钙C3AH6
6) calcium sulphoaluminate hydrate calcium aluminate sulphate hydrate
水化硫铝酸钙
补充资料：水化硫铝酸钙
分子式：
CAS号：
性质：铝酸三钙或硫铝酸钙在石膏存在时的水化产物，有高硫型和低硫型两类。若硫酸钙含量充足，则生成三硫酸盐型硫铝酸钙，其化学式为3CaO·Al2O3·3CaSO4·30～32H2O，又称钙钒石，其中铝可被铁置换，简写为AFt。若硫酸钙含量较少，则生成单硫酸盐型硫铝酸钙AFm，化学式3CaO·Al2O3·CaSO4·nH2O，其中最常见的是3CaO·Al2O3·CaSO4·12H2O，晶体为假六方板状或针尖状。密度1.99g/cm3。一轴晶负光性。一轴晶非常光折射率no=1.504，常光折射率ne=1.488。水化硫铝酸钙在快硬快凝水泥水化时是水泥石产生早期强度的主要成分。
CAS号：
性质：铝酸三钙或硫铝酸钙在石膏存在时的水化产物，有高硫型和低硫型两类。若硫酸钙含量充足，则生成三硫酸盐型硫铝酸钙，其化学式为3CaO·Al2O3·3CaSO4·30～32H2O，又称钙钒石，其中铝可被铁置换，简写为AFt。若硫酸钙含量较少，则生成单硫酸盐型硫铝酸钙AFm，化学式3CaO·Al2O3·CaSO4·nH2O，其中最常见的是3CaO·Al2O3·CaSO4·12H2O，晶体为假六方板状或针尖状。密度1.99g/cm3。一轴晶负光性。一轴晶非常光折射率no=1.504，常光折射率ne=1.488。水化硫铝酸钙在快硬快凝水泥水化时是水泥石产生早期强度的主要成分。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条