[英]['maikrəu,strʌktʃə] [美]['maɪkro,strʌktʃɚ]
组织形貌
1.
The WC-Ni ceramic coatings were prepared by detonation gun spraying with different parameters, the microstructure and worn surface of the coatings was examined by means of SEM in order to investigate the effect of parameters on the wear machanism of the coatings, it was found that a compact texture coating with high wear resistance can be obtained when the value of O_2/C_2H_2 mol ratio is about 2.
采用不同的爆炸喷涂工艺参数制备了 Ni包 WC涂层 ,用扫描电镜观察了不同工艺参数下的涂层组织与磨损面形貌 ,分析了工艺参数对涂层组织形貌及耐磨性的影响 ,结果表明 ,当比值 O2 /C2 H2 =2时 ,可获得致密的涂层 ,涂层的耐磨性能较高 ,其它条件下的涂层由于组织较疏松 ,WC颗粒在滑动摩擦时容易脱落而造成较大的磨损
2.
The overlaying processes,microstructures and oxidation resistance properties have been investigated and the results show that because of the innate brittleness of Fe 3Al,the Fe 3Al overlay with no appropriate treatment tended to crack.
通过将Fe3Al合金制成焊条 ,使用手弧堆焊 (MAS)方法 ,成功地在不锈钢基体上堆焊了Fe3Al堆焊层 ,并研究了Fe3Al合金的堆焊工艺、堆焊层的组织形貌及高温抗氧化性能。
3.
The composition and microstructure of the composite ceramic coating were analyzed by means of X-ray diffraction and scanning electron microscopy.
采用X射线衍射(XRD)、扫描电镜(SEM)分析了复合陶瓷涂层的组成及组织形貌。
5) microstructure
[英]['maikrəu,strʌktʃə] [美]['maɪkro,strʌktʃɚ]
组织形态
1.
Study on the Microstructure and Property of TC4 Alloy Joints Welded by the Electron Beam;
TC4钛合金电子束焊接接头组织形态与性能的研究
2.
The effects of microstructure,the component of oxygen and heat treatment parameters on the mechanical properties of Ti-2Al-2.
研究了组织形态、主要间隙元素O含量及热处理制度对Ti-2Al-2。
3.
X-Ray diffraction(XRD),transmission electron microscope(TEM),Auger electron spectroscopy and Raman spectroscopy had been used to investigate the microstructure and composition of the deposited films.
利用X-射线衍射仪、透射电子显微镜、俄歇电子能谱仪和拉曼光谱仪等实验手段对所沉积的TiC/a-C多层膜的组织形态、结构及成份进行了分析。
6) morphology
[英][mɔ:'fɔlədʒi] [美][mɔr'fɑlədʒɪ]
组织形貌
1.
With the help of optical microscopy and X-ray diffraction,the morphology and phase structure of the ferriteic nitrocaburized layer of M_2 high speed steel at different process has been investigated.
本文通过观察和分析M2高速钢分别在两种不同工艺下软氮化渗层的组织形貌和相结构。
2.
The morphology, diffraction pattern and the process of transformation can be investigated dynamically by differential scanning calorimetry(DSC), X-ray diffraction (XRD) and transmission electron microscopy(TEM).
通过X射线衍射(XRD)、透射电子显微镜(TEM)等方法研究了TiNi合金薄膜的组织形貌、电子衍射花样,并对其相变过程进行了动态观察。
3.
Z Theretainedausteniteofironandsteelsinthelaserhardedlayer,theirmorphology,alloyingelementsolubilityandtheirpropertieswerediscussed.
对多种钢铁材料激光处理区中的残留奥氏体的组织形貌、合金元素固溶度及其各种性质进行了讨论。