1) anatase titanium dioxide
锐锥石型钛白粉
2) rutile titanium white powder
金红石型钛白粉
1.
Investigation of use performance of rutile titanium white powder in water-borne coatings
金红石型钛白粉在水性涂料中应用性能的探讨
3) anatase titan white
锐钛矿型钛白
4) Andtase-Ru-tile transformation
锐钛型一金红石型转化
5) anatase
[英]['ænə,teis] [美]['ænə,tes]
锐钛矿型
1.
In-situ growth of anatase nano-TiO_2 on cotton fabric and its UV screening property;
锐钛矿型纳米TiO_2在棉织物上的原位生长及其抗紫外线性能
2.
One-step Synthesis of Anatase-Crystalline Titania Hollow Spheres in Aqueous Solution;
水相一步合成锐钛矿型二氧化钛空心球
3.
Then anatase nano-TiO2 powder was calcined at the temperature between 400~1 000 ℃.
在400～1 000℃之间对锐钛矿型TiO2进行煅烧,分析了不同温度处理后样品的晶体结构和光催化活性的变化。
6) anatase
[英]['ænə,teis] [美]['ænə,tes]
锐钛型
1.
The regular cube-shaped particles with uniform particle size is about 200 nm with single crystal structure of anatase phase.
其形貌规整,尺寸分布窄,都在200 nm左右,且相结构为锐钛型单晶。
2.
The results showed that TiO_2 was anatase with high thermal stability,the surface area was 121 m~2·g~(-1),the mean grain size of crystal was 13 nm,the mean pore size was 10 nm,the mean grain size of nanoparticles was le.
采用沉淀法,以水溶液为反应体系,无机物(硫酸氧钛和氢氧化钠)为主要原料,加入少量模板剂,制备出锐钛型介孔纳米二氧化钛粉体。
3.
The results show that the crystal phase of mesoporous TiO_2 is anatase with high heat stability,the surface area is 121 m~2/g,the mean grain size of crystal is 12 nm,the mean pore size is 10 nm and .
采用沉淀法,以水溶液为反应体系,无机物(硫酸氧钛和氢氧化钠)为主要原料,加入少量模板剂,制备出了锐钛型介孔纳米二氧化钛粉体,并对产物的生成机理进行了探讨。
补充资料：锐钛矿型钛白
分子式：
CAS号：
性质：以锐钛矿型二氧化钛为主成分的白色颜料。白色粉末二氧化钛含量95%～99%，折射率2.55，密度3.70～3.85g/cm3。吸油量20～24，着色力1300～1350。平均晶体颗粒0.14～0.15μm，比表面积10～14m2/g，莫氏硬度5.5～6，比热容0.71J/(℃·g)。耐化学品，耐高温。
CAS号：
性质：以锐钛矿型二氧化钛为主成分的白色颜料。白色粉末二氧化钛含量95%～99%，折射率2.55，密度3.70～3.85g/cm3。吸油量20～24，着色力1300～1350。平均晶体颗粒0.14～0.15μm，比表面积10～14m2/g，莫氏硬度5.5～6，比热容0.71J/(℃·g)。耐化学品，耐高温。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。