1) striking,temperature
乳浊化温度
2) Clouding temperature
浊化温度
3) emulsifying temperature
乳化温度
1.
This paper introduces the preparation of waterborne bisphenol A epoxy resin emulsion by phase inversion and investigates the effects of such factors as surfactant type and amount,emulsifying temperature,resin molecular weight and solvent type on the particle size and stability of epoxy emulsion.
介绍了使用相反转法制备双酚A型环氧树脂水基乳液,研究表面活性剂类别及其用量、乳化温度、树脂分子量、溶剂的种类等各种因素对环氧树脂乳液颗粒度大小和稳定性的影响。
2.
Effects of emulsifying temperature and adding time of complex emulsifier into the liquid rosin system on emulsification efficiency,sizing performance of the third-grade rosin based cationic dispersed rosin size were investigated in this paper.
采用常压逆转工艺制备出了性能优良的阳离子微粒乳化中性分散松香胶,对制备过程中乳化温度、复合乳化剂的加入时间进行了探讨,实验结果表明,在综合考虑操作成本与乳化效果的前提下,乳化温度以140℃为宜,复合乳化剂的加入时间以20m in为宜。
4) opacity
[英][əʊ'pæsəti] [美][o'pæsətɪ]
乳浊度
5) opacimeter
[,əupə'simitə]
乳浊度计
6) cloudy agent
乳浊(化)剂
补充资料：乳浊釉
分子式：
CAS号：
性质：又称盖地釉。陶瓷坯体上不透明的玻璃状覆盖层。以普通透明釉为基础添加乳浊剂而构成。产生乳浊效果的原因是乳浊剂粒子与透明釉的玻璃体对光的折射率不同，引起光散射所致。两者折射率差别愈大，乳浊程度愈高。常用乳浊剂有锆英石、二氧化锡、二氧化钛、二氧化铈、二氧化锆等。其中锆英石资源丰富，成本低。乳浊作用还可以用釉层的玻璃相出现分相，即一种为基础玻璃，另一种为分散的玻璃相微粒，两者化学组成和折射率不同，也可产生光散射而引起乳浊，称为“乳光”。当釉层中含大量微细气泡时也可形成乳浊，古瓷中青瓷釉的乳浊性主要是这种气相乳浊作用。乳浊釉已广泛应用于建筑卫生陶瓷制品，可以掩盖住坯体的杂色和缺陷。
CAS号：
性质：又称盖地釉。陶瓷坯体上不透明的玻璃状覆盖层。以普通透明釉为基础添加乳浊剂而构成。产生乳浊效果的原因是乳浊剂粒子与透明釉的玻璃体对光的折射率不同，引起光散射所致。两者折射率差别愈大，乳浊程度愈高。常用乳浊剂有锆英石、二氧化锡、二氧化钛、二氧化铈、二氧化锆等。其中锆英石资源丰富，成本低。乳浊作用还可以用釉层的玻璃相出现分相，即一种为基础玻璃，另一种为分散的玻璃相微粒，两者化学组成和折射率不同，也可产生光散射而引起乳浊，称为“乳光”。当釉层中含大量微细气泡时也可形成乳浊，古瓷中青瓷釉的乳浊性主要是这种气相乳浊作用。乳浊釉已广泛应用于建筑卫生陶瓷制品，可以掩盖住坯体的杂色和缺陷。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。