1) fused salt extracrion
熔融盐萃取
2) fused-salt extraction
熔盐萃取
1.
During fused-salt extraction,one time to produce low oxygen and low fluorine dysprosium metal by the combining method of calcium reducing agent and fused-salt extractionare used.
9%;采用钙热还原及熔盐萃取联合法一次性制备工艺,可有效降低金属镝中的氧、氟含量,制备的金属镝纯度大于99。
2.
In this paper, the research that the hypoxia and hypocalcia rare-earth metals (Dysprosium, Yttrium) are prepared by fused-salt extraction method is mainly developed.
本文主要开展了用熔盐萃取法制备低氧、低钙的高纯稀土金属(Dy、Y)的研究。
3) molten salt extraction
熔盐萃取
1.
It is conventionally difficult to obtain metallic lithium with ultra low Na/K content,to which the molten salt extraction is therefore suggested as a pioneer process to remove Na/K and relevant experiments.
探索性实验结果表明,熔盐萃取法可除去金属锂中的钠和钾,尤其是除钾效果比较明显,这与热力学分析结果基本吻合。
4) molten bismuth extraction
熔融铋萃取
6) molten silver extraction process
熔融银萃取法
补充资料：为再结合熔融石英制品、熔融石英陶瓷制品
分子式：
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。