2) fused electrolytic iron
熔融电解铁;熔铸电解铁
3) bath smelting reduction process
铁浴熔融还原
1.
The pilot test of bath smelting reduction process producing stainless master alloy was carried out in a 15 t complex blowing converter.
在15t复吹转炉中进行了不锈钢母液的铁浴熔融还原工业试验，发现铬的收得率不高，且母液含磷过多。
4) iron bath smelting reduction process
铁浴熔融还原法
1.
This paper proposes a new pyrometallurgical process for treating zinc oxide ore iron bath smelting reduction process, and describes the experimental investigation of the process after analysis of its principle; the zinc oxide dust thus produced contains 95~98% ZnO, 1 6~2 5% PbO, and the zinc volatilization rate is higher than 93%.
提出了氧化锌矿火法处理的新工艺——铁浴熔融还原法 ,分析了其工艺原理 ,用该工艺试验研究制得的锌氧粉 w Zn O95 %～ 98% ,w Pb O1。
5) Softening Iron Ore Melting
铁矿石软化熔融
6) Smelting reduction ironmaking technology
熔融还原炼铁技术
补充资料：为再结合熔融石英制品、熔融石英陶瓷制品
分子式：
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。
CAS号：
性质：又称为再结合熔融石英制品、熔融石英陶瓷制品或石英玻璃烧结制品。具有良好的化学稳定性。抗酸性和抗冲刷性强。高温机械强度大。热膨胀系数低。气孔率低。导电率低。但在1100℃以上长期使用时，制品中的石英会向方石英转变，使制品产生裂纹和剥落。以熔融石英为原料，经粉碎、成型、干燥、烧成而制得。制法有泥浆浇注法、蜡注法、捣打法、半干压法和等静压成型等。由于在烧成时收缩小，可以制得尺寸精确的制品。可用于制作耐酸容器、反应罐内衬耐酸部件等。冶金工业中用其制成浸入式水口，使用效果很好。