1)  heat treatment protective coating
热处理保护涂层
2)  heat treatment protecting coating
热处理保护涂料
3)  heat treatment protective coating
热处理保护层
4)  refractory protection
耐热保护层,耐热涂层
5)  Protective Coating
保护涂层
1.
Taking GCr15 steel billets for test material,a uniform protective coating was covered on the billets before loading into the blast furnace.
结果表明 ,保护涂层对减少GCr15钢表面脱碳层有明显效果。
2.
This paper deals with the compostion of pasty boronization of steel with protective coating.
本研究对膏剂渗硼用保护涂层的组成进行了优选,优选出的配方保护效果良好,涂层材料价廉易得,来源广。
3.
Through using the self-designed loading device,the permeability of coating concrete chloride ion with concrete protective coating and different brush coating times has been researched in this paper.
本文利用自行设计的加载设备对混凝土保护涂层及涂层涂刷次数等不同情况下的氯离子渗透性进行了研究。
6)  protection coating
保护涂层
1.
A review was given on the progress of research on the protection coating prepared by sol-gel method.
溶胶凝胶(Solgel)法用于金属及合金表面制备保护涂层可明显提高材料在各种环境下的耐蚀性、抗高温氧化性、耐磨性等性能,从而扩大金属及其合金的应用范围。
补充资料:金属热处理 :感应加热热处理
        用感应电流使工件局部加热的表面热处理工艺。这种热处理工艺常用於表面淬火﹐也可用於局部退火或回火﹐有时也用於整体淬火和回火。20世纪30年代初﹐美国﹑苏联先后开始应用感应加热方法对零件进行表面淬火。随著工业的发展﹐感应加热热处理技术不断改进﹐应用范围也不断扩大。
         基本原理 将工件放入感应器(线圈)内(图1 感应加热原理 )﹐当感应器中通入一定频率的交变电流时﹐周围即產生交变磁场。交变磁场的电磁感应作用使工件内產生封闭的感应电流──涡流。感应电流在工件截面上的分布很不均匀﹐工件表层电流密度很高﹐向内逐渐减小(图2 沿工件截面的电流密度分布 )﹐这种现象称为集肤效应。工件表层高密度电流的电能转变为热能﹐使表层的温度昇高﹐即实现表面加热。电流频率越高﹐工件表层与内部的电流密度差则越大﹐加热层越薄。在加热层温度超过钢的临界点温度后迅速冷却﹐即可实现表面淬火。
         分类 根据交变电流的频率高低﹐可将感应加热热处理分为超高频﹑高频﹑超音频﹑中频﹑工频 5类。①超高频感应加热热处理所用的电流频率高达27兆赫﹐加热层极薄﹐仅约0.15毫米﹐可用於圆盘锯等形状复杂工件的薄层表面淬火。②高频感应加热热处理所用的电流频率通常为200~300千赫﹐加热层深度为0.5~2毫米﹐可用於齿轮﹑汽缸套﹑凸轮﹑轴等零件的表面淬火。③超音频感应加热热处理所用的电流频率一般为20~30千赫﹐用超音频感应电流对小模数齿轮加热﹐加热层大致沿齿廓分布﹐粹火后使用性能较好。④中频感应加热热处理所用的电流频率一般为2.5~10千赫﹐加热层深度为2~8毫米﹐多用於大模数齿轮﹑直径较大的轴类和冷轧辊等工件的表面淬火。⑤工频感应加热热处理所用的电流频率为50~60赫﹐加热层深度为10~15毫米﹐可用於大型工件的表面淬火。(见彩图 差温炉淬火600毫米直径冷轧辊工频感应加热淬火大型铸钢件的热处理炉真空淬火炉 )