1) methyl cyanoacrylate
氰基丙烯酸甲酯
2) Methyl-2-cyanoacrylate
2-氰基丙烯酸甲酯
3) Methyl-2-cyanoacrylate
α-氰基丙烯酸甲酯
4) mecrylate
氰丙烯酸甲酯
5) α-cyanoacrylate
α-氰基丙烯酸酯
1.
Present status and prospect ofα-cyanoacrylate instant adhesive;
α-氰基丙烯酸酯瞬间胶粘剂的现状和展望
2.
Study on Synthesis Technique and Modification of α-Cyanoacrylate;
α-氰基丙烯酸酯合成及改性工艺的研究
3.
α-Cyanoacrylate:An effective adhesive agent for corneal perforation in rabbits;
α-氰基丙烯酸酯用于兔角膜穿通伤的研究
6) polybutylcyanoacrylate
聚氰基丙烯酸酯
1.
The Research on IR and TEM of Polybutylcyanoacrylate Nanoparticles;
聚氰基丙烯酸酯纳米颗粒的红外光谱及相关分析
2.
Though the latex polymerization,the polybutylcyanoacrylate nanoparticles with the approximate size of 200 nm are prepared.
采用乳液聚合的方法制备直径200 nm左右的聚氰基丙烯酸酯纳米颗粒,利用透射电镜和X射线能谱仪研究聚氰基丙烯酸酯纳米颗粒自组装的影响因素。
3.
Though the latex polymerization with stability (Dextran),the polybutylcyanoacrylate nanoparticle with a size significantly approximately 200nm is preduced.
采用乳液聚合的方法可获得直径200 nm 左右的聚氰基丙烯酸酯纳米颗粒。
补充资料：2-氰基丙烯酸甲酯
分子式：C5H5NO2
分子量：111.10
CAS号：137-05-3
性质：无色液体。沸点为47-48α（0.267kPa），相对密度1.1044（27/4℃），折光率1.443（25℃）。溶于乙醚、氯仿、甲氯化碳、苯、二氧六环，不溶于甲醇、乙醇、露置空气中逐渐聚合。
制备方法：由氰乙酸甲酯经聚合、裂解而得。将氰乙酸甲酯（见24530）和哌啶混合，加入预热至80℃的甲醛中。保温搅拌反应1h，将反应液放入冰水中，经球磨、粉碎、洗涤、干燥得聚2-氰基丙酸甲酯。将其与对苯二酚、五氧化二磷、磷酸三甲酚加入反应锅，保持微负压通入二氧化硫，加热到230℃裂解。裂解产物再加入对苯二酚、五氧化二磷及二氧化硫，减压蒸馏，收集80℃（0.67kPa）馏分，即得2-氰基丙烯酸甲酯。该品需加入0.01%对苯二酚密封保存。
用途：该品具有片刻聚合的特点，有强大的粘着力，用作胶粘剂和聚合物的单体，可用于皮肤手术切口和新鲜伤口的粘合。
分子量：111.10
CAS号：137-05-3
性质：无色液体。沸点为47-48α（0.267kPa），相对密度1.1044（27/4℃），折光率1.443（25℃）。溶于乙醚、氯仿、甲氯化碳、苯、二氧六环，不溶于甲醇、乙醇、露置空气中逐渐聚合。
制备方法：由氰乙酸甲酯经聚合、裂解而得。将氰乙酸甲酯（见24530）和哌啶混合，加入预热至80℃的甲醛中。保温搅拌反应1h，将反应液放入冰水中，经球磨、粉碎、洗涤、干燥得聚2-氰基丙酸甲酯。将其与对苯二酚、五氧化二磷、磷酸三甲酚加入反应锅，保持微负压通入二氧化硫，加热到230℃裂解。裂解产物再加入对苯二酚、五氧化二磷及二氧化硫，减压蒸馏，收集80℃（0.67kPa）馏分，即得2-氰基丙烯酸甲酯。该品需加入0.01%对苯二酚密封保存。
用途：该品具有片刻聚合的特点，有强大的粘着力，用作胶粘剂和聚合物的单体，可用于皮肤手术切口和新鲜伤口的粘合。