Contrast analyzing to wrinkle of sheet metal in the multi-point forming and whole-die forming;
薄板件多点成形与模具成形时起皱现象的对比分析
2.
Numerical Analysis of Wrinkle and Springback in Multi-point Forming for Sheet Metal;
板材多点成形中起皱和回弹的数值分析
3.
Circular angle wrinkles in the bottom,wrinkles in the mouth,vertical wrinkles in the side wall,U-shaped and wrinkles in some area of bottom during deep drawing of a stainless thin wall part.
介绍了在制造一种深筒薄壁不锈钢拉深件中遇到的几种工件底部圆角起皱、口部起皱、侧壁纵向皱折、工件呈马蹄形、底部局部起皱现象和对零件进行表面观察、解剖分析,查找产生问题的原因,以及通过修整模具、调整间隙、选择变形系数等措施加以解决的经验和方法。
5) wrinkling
起皱
1.
Prediction of wrinkling and crack during multi-point drawing forming process for rectangle cup with conical walls;
斜壁盒形件多点拉延成形过程中起皱与拉裂预测
2.
The Influence of blank shape and the setting of drawbead on wrinkling and inadequate stretch areas in automobile covering parts forming processes;
板料形状、压料筋的设置对汽车覆盖件成形中起皱和未充分拉深的影响
3.
Cause of Wrinkling in SUS430 Stainless Steel Sheets and Effect of Solidified Structure on Wrinkling;
SUS430不锈钢薄板起皱缺陷的成因及凝固组织对它的影响
6) crinkling
起皱
1.
Reasons of cylindric spare parts crinkling during extending and preventment measures;
圆筒形引伸零件的起皱原因及预防措施
2.
The problem of crinkling is fatal in the drawing process.
在冲压拉延过程中 ,存在着一个严重的工艺问题——起皱 ,防止起皱的主要措施是在拉延模具上增设压边机构。
参考词条
补充资料：酚醛烘干皱纹漆
分子式：
CAS号：
性质：以酚醛树脂为主要成膜物质的一类装饰性烘漆。由酚醛树脂、颜料、干性油、催干剂和有机溶剂制造而成。该漆烘烤后，漆膜坚硬，皱纹美观，分粗、中、细三种皱纹。适用各种仪器、仪表、文教用具、小五金零件等装饰保护，可遮蔽底材的不平整。
CAS号：
性质：以酚醛树脂为主要成膜物质的一类装饰性烘漆。由酚醛树脂、颜料、干性油、催干剂和有机溶剂制造而成。该漆烘烤后，漆膜坚硬，皱纹美观，分粗、中、细三种皱纹。适用各种仪器、仪表、文教用具、小五金零件等装饰保护，可遮蔽底材的不平整。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。