1) vibration strength
耐振强度
2) vibration resistance strenth
耐振度
1.
The concept of vibration resistance strenth is also advanced.
综述了破损边界理论及用Ｄｕｈａｍｅｌ积分得到的几种典型脉冲的冲击谱公式和破损边界曲线，提出了产品耐振度的概念。
3) compressive strength
耐压强度
1.
The effects of different temperatures on compressive strength and bulk density were studied.
主要探讨了不同的烧结温度对试样的耐压强度和体积密度的影响。
2.
A test is done on pre-baked anode made from calcined coke in aspects of apparent density,real density,porosity,resistivity of powder,compressive strength,which shows compressed petroleum coke improves its chemical and physical performances.
采用压密煅烧石油焦制成预焙阳极,通过体积密度、真密度、显气孔率、电阻率、耐压强度、透气度的测试,结果表明,压密石油焦能显著地改善预焙阳极的理化性能,使预焙阳极制造过程中沥青加入量控制在13%,预焙阳极的体积密度达到1。
3.
In order to save the required energy for grinding the slag, the compressive strength of the slag is reduced by inducing cracks in it with the help of microwave.
为研究引发的裂纹对碾磨渣的影响,对经过微波处理的高钛高炉渣进行了耐压强度测试。
4) crushing strength
耐压强度
1.
These physical properties were correlated with the crushing strength of unglazed-fired tiles.
论述了从塞拉利昂不同地区采集的６个粘土试样的一些物理性能，这些物理性能与无釉烧结地砖的耐压强度有一定的关系。
5) cold crushing strength
耐压强度
1.
Support vector machine, a new computational method that have powerful prediction ability and can avoid over-fitting, has been used for optimizing processing parameters (content, particle size, and firing temperature of added silicon) in the preparation of alumina-carbon material and establishing the model of their influence on cold crushing strength of samples.
通过实验数据处理,建立了金属硅粒度、含量和热处理温度与烧后冷态耐压强度的数学模型。
2.
Based on the production data of 1997 s,the regression equation of the relationship among cold crushing strength,volume density and granular conformation of magnesitecarbon bricks is obtained.
利用１９９７年生产数据建立数学模型，得到镁碳砖的耐压强度、体积密度与颗粒组成关系的回归方程，并利用回归方程进行预测，为生产高强度镁碳砖，提高原料利用率，选择优良配方，提供了理论依
6) compression strength
耐压强度
1.
The results show that: the fillers of SiO_2 based investment consist of SiO_2,Al_2O_3 and MgO,and the binder is NH_4H_2PO_4;for SiO_2 based investment,the bulk density and the compression strength decrease,the apparent porosity and the thermal expansion increase,when the specimens are heated to 900 ℃;the fil.
结果表明:氧化硅系包埋料的骨料是氧化硅、氧化铝、氧化镁,结合剂为磷酸二氢铵,其900℃煅烧后显气孔率增加,体积密度下降,耐压强度降低,热膨胀增大;氧化铝系包埋料的骨料是氧化铝和氧化镁,结合剂为磷酸二氢铵,其900℃烧后显气孔率增加,体积密度下降,热膨胀变化不大;氧化镁系包埋料的骨料是氧化镁和氧化铝,结合剂是铝酸钙水泥,其900℃烧后耐压强度明显降低,热膨胀明显增大。
2.
According to the geometrical structure of the elbow-rubber hose reinforced by spiraled cords threads, its calculation formulation of compression strength is derived on the base of the stress analysis with the inner-pressure.
在肘形橡胶软管内压作用下的应力分析的基础上,根据其几何结构,推导出帘线缠绕增强肘形橡胶软管耐压强度计算公式,分析结果表明:帘线缠绕增强肘形橡胶软管弯管段爆破压力低于直管段爆破压力,因此其耐压强度只需根据弯管段爆破压力进行评估。
补充资料：振子强度
表征原子的吸收或发射的重要物理参数。经典电动力学把辐射或吸收的基本单元看作是谐振子。电磁波的发射或吸收是由谐振子作简谐运动引起的。由此可以计算出一个振子的吸收系数。在确定的谱线内通常把一个原子的吸收作用用等效的振子数表达，这个数就叫作振子强度,常用f来表示。fik表示从分立能级i跃迁到k的振子强度。已知振子强度，就可求出原子吸收系数。振子强度可以通过两条途径求出：理论计算和实验测定。根据振子强度和原子的跃迁几率之间的关系进行理论计算，可以得到
，
式中Aki为爱因斯坦自发跃迁几率,gi、gk分别为谱线低能级i和高能级k的统计权重,e和me为电子电量和质量，c为光速，v为谱线频率。Aki可以利用量子力学方法计算。一般说来,对较轻的原子,计算所得的结果是满意的。对比较重的原子，Aki的计算是比较困难的；因此，曾用多种方法进行实验测定；不过，目前可测的范围还是很有限的。此外，也可以利用太阳或有比较准确的物理参量的恒星的生长曲线，去反求一些谱线的振子强度值。
，
式中Aki为爱因斯坦自发跃迁几率,gi、gk分别为谱线低能级i和高能级k的统计权重,e和me为电子电量和质量，c为光速，v为谱线频率。Aki可以利用量子力学方法计算。一般说来,对较轻的原子,计算所得的结果是满意的。对比较重的原子，Aki的计算是比较困难的；因此，曾用多种方法进行实验测定；不过，目前可测的范围还是很有限的。此外，也可以利用太阳或有比较准确的物理参量的恒星的生长曲线，去反求一些谱线的振子强度值。