1) lead oxide molybdate crystal
钼酸二铅晶体
2) PbMoO 4 wafer
钼酸铅晶体
1.
Compared with the conventional thermal vapor deposition coating, the ion assisted deposition technology is particularly helpful for the infrared antireflection coating on PbMoO 4 wafer that requires higher coating quality and greater position accuracy of the center wavelength.
通过与常规的热蒸发工艺镀制的膜层相比较 ,证实了离子束辅助沉积技术有助于提高钼酸铅晶体表面红外增透膜的膜层品质及中心波长位置的精确度。
3) lead molybdate single crystal
钼酸铅单晶
4) ammonium dimolybdate crystal
二钼酸铵晶体
1.
Raman spectrum of saturated aqueous solution of ammonium dimolybdate crystal was recorded, and compared with those of ammonium dimolybdate crystal, ammonium heptamolybdate crystal, saturated aqueous solution of ammonium heptamolybdate crystal and monomolybdate anion in aqueous solution respectively.
记录了常温下二钼酸铵晶体饱和水溶液的Raman光谱,并分别与二钼酸铵晶体、仲钼酸铵晶体、仲钼酸铵晶体饱和水溶液、水溶液状态下单钼酸根离子的Raman光谱进行了比较研究。
5) Non-agglomerating crystal formation
非团聚二钼酸铵晶体
6) molybdate crystals
钼酸盐晶体
1.
The Al13 based molybdate crystals with multimorphologies were synthesized via a direct mixing and aging method.
以H3PMo12O4·0nH2O、H4PMo11VO4·0nH2O和(NH4)6P2Mo18O6·2nH2O3种杂多化合物为钼源,采用直接混合后陈化的方法合成了多形貌A113基钼酸盐晶体,相应A113基钼酸盐晶体的形貌和尺寸分别是斜方三棱柱形(80μm×30μm)、星形(30μm×10μm)和叶片形(500μm×150μm)。
补充资料：钼酸钆晶体
分子式：Gd2(MoO4)3
CAS号：
性质：具有畴结构的三价稀土金属钼酸盐的一种。Α钼酸钆是热力学稳定相，而β钼酸钆在室温下是热力学近稳态相。后者在居里点（159℃）以下既有铁电性又有铁弹性。在居里点以上，铁电性和铁弹性皆没有。但有压电性，结构上变成反铁电性。属于三维型铁电体。钼酸钆晶体的介电性，铁弹性、压电系数都比较小。在室温下，光学上是双轴晶体，化学上稳定，不溶于水。β钼酸钆的熔点为1170℃，从熔体中用提拉法制取晶体，单晶呈无色透明，可用于制造λ/4，λ/2波长片、激光快门、色相调制元件和间隔调制器等元件。
CAS号：
性质：具有畴结构的三价稀土金属钼酸盐的一种。Α钼酸钆是热力学稳定相，而β钼酸钆在室温下是热力学近稳态相。后者在居里点（159℃）以下既有铁电性又有铁弹性。在居里点以上，铁电性和铁弹性皆没有。但有压电性，结构上变成反铁电性。属于三维型铁电体。钼酸钆晶体的介电性，铁弹性、压电系数都比较小。在室温下，光学上是双轴晶体，化学上稳定，不溶于水。β钼酸钆的熔点为1170℃，从熔体中用提拉法制取晶体，单晶呈无色透明，可用于制造λ/4，λ/2波长片、激光快门、色相调制元件和间隔调制器等元件。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。