1) iron sulfide film
硫化铁膜
2) pyrite thin film
二硫化铁薄膜
1.
About 500?nm thick Fe thin films were deposited on the glass substrate by thermal evaporation firstly,and then they were sulfurized at different temperatures to synthesize pyrite thin films.
采用真空热蒸发法在玻璃基片上沉积厚度约为500 nm的铁膜,然后对铁膜在温度为553~673 K的条件下恒温硫化6 h,以制备二硫化铁薄膜。
2.
In this paper, the research progress of pyrite thin films has been reviewed from the research results.
本文从不同制备方法所制备出的二硫化铁薄膜的研究结果,分析二硫化铁薄膜的研究现状。
3) iron sulfides
硫铁化物
1.
This paper is aimed at introducing the authors' research of the spontaneous combustion characteristics of iron sulfides as a result of the reactions of hydrogen sulfide to the different degrees of humidity of the iron oxide black, iron oxide red and the iron hydroxide.
通过模拟储油罐中硫铁化物的生成方式,分析和研究了H2S气体在无氧条件下,与不同相对湿度的Fe2O3、Fe3O4和Fe(OH)3反应所生成的硫铁化物的自燃性。
2.
The oxidation heat of the iron sulfides is regarded as the main cause of tank fire.
油品储罐中的H2S气体在没有O2的室温条件下能与储罐内壁铁的主要腐蚀产物Fe2O3发生化学反应生成硫铁化物,硫铁化物的氧化放热是引起含硫油品储罐着火的主要原因。
3.
Self-ignition accident by sour oil tank was analyzed,and the major reason was found to be thermal oxidation of iron sulfides generated from reaction of rust with hydrogen sulfide.
通过对含硫油品储罐自燃事故的分析发现,储罐内壁铁锈与活性硫(主要为H2S)反应,生成的硫铁化物的氧化放热是导致自燃的主要原因。
4) ferrous sulfide
硫化亚铁
1.
Recovering arsenic from waste acid water with ferrous sulfide in producing vitriol;
利用硫化亚铁从污酸废水中回收砷
2.
A Study of Pyrophoric Nature of Ferrous Sulfide;
硫化亚铁自燃特性的研究
5) iron sulfide
硫化铁
1.
Spontaneous combustion tendency of iron sulfide in natural environment;
自然环境条件下硫化铁的自燃倾向性
2.
Oxidation experiment was made on iron sulfide by spontaneous ignition test system to explore the spontaneous combus- tion tendency of iron sulfide in natural environment.
采用自然氧化实验系统,在自然条件下,对Fe_3O_4、Fe_2O_3以及Fe(OH)_3的混合物硫化后生成的硫铁化合物进行氧化实验,研究硫化铁在自然环境中的自燃倾向性。
3.
The preparation and catalytic performances for thermochemical decompositionreaction of H_2S to H_2 of several catalysts of iron sulfide were investigated.
用不同方法制备了几种硫化铁催化剂，研究了其对Ｈ＿２Ｓ分解制取氢气反应的催化性能。
6) iron sulfide
硫化亚铁
1.
Research of functions of detergent YX-LS5 for iron sulfide;
YX-LS5硫化亚铁清洗剂性能的研究
2.
Research on composite cleaning agent of iron sulfide
复合型硫化亚铁清洗剂的研究进展
3.
Synergistic treatment of iron sulfide laden and stabilized slops simultaneously by use of surfactant and denitrifying bacteria was studied.
对表面活性剂和反硝化细菌协同处理含硫化亚铁颗粒污油的可行性进行了研究。
补充资料：二硫化铁
分子式：FeS2
CAS号：
性质：黄色立方晶体。熔点1171℃。密度5.0g/cm3。黄铁矿的主要成分。有反磁性。室温为非活性物质。温度升高后变得活泼。在空气中氧化成三氧化二铁和二氧化硫。主要用于制造硫酸。
CAS号：
性质：黄色立方晶体。熔点1171℃。密度5.0g/cm3。黄铁矿的主要成分。有反磁性。室温为非活性物质。温度升高后变得活泼。在空气中氧化成三氧化二铁和二氧化硫。主要用于制造硫酸。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。