1) bonderized
磷化处理的
2) phosphating treatment
磷化处理
1.
Phosphating treatment and blackening treatment as two different ways have been used and the microstructure and the microhardness have been analyzed under different pretreatment craft.
实验结果表明:磷化和黑化处理都可以提高材料表面的激光吸收率,但磷化处理更容易控制具体参数;在相同的激光功率和扫描速度下,经过磷化工艺预处理的处理层厚度比未经预处理的处理层提高了0。
3) Phosphating
['fɔsfeitiŋ]
磷化处理
1.
The phosphating solutions were developed to prepare phosphating films on NdFeB permanent magnet so as to increase the corrosion resistance.
为了提高NdFeB磁体的耐蚀性,并验证磷化膜的组成,以自制的磷化液在NdFeB永磁体表面进行磷化处理,并采用SEM观测了采用不同表调剂处理NdFeB永磁体表面所形成的磁化膜微观形貌,测试分析了磷化膜的抗腐蚀性能;采用EDS、XRD、ICP-AES等对磷化膜进行了研究。
2.
This paper proposes a new anticorrosive process of phosphating instead of the traditional process of zincification to improve the ability of corrosion prevention of windscreen wiper.
研究了采用磷化处理工艺代替传统的镀锌工艺以提高汽车刮水器弹簧的防腐能力。
3.
Superfine manganese phosphate conversion coating was prepared on the surface of 20Cr by phosphating.
采用新型磷化处理工艺在20Cr钢表面制备了超微细磷酸锰转化涂层。
4) Phosphate Treatment
磷化处理
1.
Effect of external magnetic fields on phosphate treatment on high-speed steel is significant: promoting the building of phosphate film and greatly improving the appearance and composition of the film.
即一定强度的磁场可以降低磷化处理系统的熵值,加速磷化盐膜的形成。
5) phosphatizing
磷化处理
1.
Experimental Research of Phosphatizing to High-speed Steel Tool;
高速钢刀具磷化处理试验研究
补充资料：磷化处理
分子式：
分子量：
CAS号：
性质：在钢铁制件表面上生成一层不溶性磷酸盐（包括磷酸铁、磷酸锰和磷酸锌）保护膜的过程。用于提高抗蚀性和绝缘性，并作为油漆底层。通常将制件浸入硝酸锌和马日夫盐[即磷酸铁锰χFe(H2PO4)2·yMn(H2PO4)2]所配成的溶液中进行磷化，使制件表面上形成一薄层灰黑色、细结晶和多孔性的磷化膜。加入硝酸盐等可溶性氧化剂，可促进发生沉积作用。加入硫化锌或硝酸钙，可产生黑色表面。然后再浸渍重铬酸钾溶液和锭子油，或涂上清漆、磁漆进行封闭。磷化处理操作简单而价廉，广泛用于保护钢铁制品，免受大气腐蚀。
分子量：
CAS号：
性质：在钢铁制件表面上生成一层不溶性磷酸盐（包括磷酸铁、磷酸锰和磷酸锌）保护膜的过程。用于提高抗蚀性和绝缘性，并作为油漆底层。通常将制件浸入硝酸锌和马日夫盐[即磷酸铁锰χFe(H2PO4)2·yMn(H2PO4)2]所配成的溶液中进行磷化，使制件表面上形成一薄层灰黑色、细结晶和多孔性的磷化膜。加入硝酸盐等可溶性氧化剂，可促进发生沉积作用。加入硫化锌或硝酸钙，可产生黑色表面。然后再浸渍重铬酸钾溶液和锭子油，或涂上清漆、磁漆进行封闭。磷化处理操作简单而价廉，广泛用于保护钢铁制品，免受大气腐蚀。