1) interparticle fracture
粒间断裂
2) inter-particle rupture
颗粒间断裂
1.
The "black powder" could be found in Ni-based superalloy powder produced by plasma rotation electrode process(PREP),The effects of "black powder" on formation of previous particle boundary(PPB),inter-particle rupture and mechanical properies of PM superalloy were studied.
研究了用等离子旋转电极(PREP)工艺生产的镍基高温合金粉末中发现的“黑粉”及其对PM合金中形成原始颗粒边界(PPB)等异常组织,并在力学试验中造成颗粒间断裂和对性能的影响。
2.
The result shows that,the PPB is a direct factor to form inter-particle rupture.
通过对直接热等静压成形的粉末冶金高温合金力学试验断口的观察分析,阐述了粉末颗粒间断裂的形貌特征及对力学性能的影响。
3) Inter-grain spacing
磨粒间距
4) interparticle distance
粒间距
5) interparticle forces
粒间力
6) interparticle spacing
颗粒间距
参考词条
补充资料：晶间断裂
intergranularfracture：沿着晶粒界间发生的断裂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。