1) blue brittleness,blue shortness
蓝脆性
2) blue brittleness
蓝脆
1.
By the manufacture instance of two drawing parts namely petrol cover and end cover, the reasons occurring drawing crack defect during manufacture are analyzed separately, the occurring of blue brittleness and hydrogen brittleness during drawing are introduced, as well as related solving and guarding steps are provided.
通过油盖及端盖两种拉伸件的加工实例,分别分析了其在生产中出现拉裂缺陷的原因,由此介绍了拉伸加工中蓝脆与氢脆的产生并分别提出了各自的解决及预防措施。
2.
However, at the temperature about 230℃, the sensibilities to stress corrosion increase abruptly, blue brittleness occurs and the stress corrosion is increased.
通过对不同强度等级的汽轮机转子钢进行应力腐蚀试验,研究发现,转子钢在一般水介质中应力腐蚀敏感性很小,但在230℃附近应力腐蚀敏感性突然增加,这可能是发生了蓝脆,增加了应力腐蚀。
3.
30Cr2Ni4MoV and 30Cr2MoV steels presented blue brittleness near 230℃ and 180℃, respectively.
本文研究了核电汽轮机用钢蓝脆和应力腐蚀的交互作用，结果表明：这类中强度钢在水介质中的应力腐蚀敏感性很小，只能用慢拉伸方法才能发现。