1) crimp modulus
卷曲模量
3) crimping capacity
卷曲容量
5) flexural modulus
弯曲模量
1.
Preparation and flexural modulus of biodegradable composites reinforced with kenaf fibers;
洋麻纤维增强全降解复合材料的制备及其弯曲模量
2.
Biodegradable composites reinforced with bagasse fibre were prepared by a press forming,and the thermal properties of fibre and the flexural modulus of composites were investigated in view of the fibre content and length.
利用压制成型制备了甘蔗渣纤维增强可降解复合材料,分析了纤维的热分解性能,研究了纤维含有量和纤维长度对材料弯曲模量的影响,利用Cox剪滞法和材料的结构特点,探讨了一种新的修正模型对弯曲模量的预测。
3.
The flexural strength and flexural modulus will reach the maximum value of 130 MPa and 4.
分别研究了丙烯腈基短切碳纤维含量、引发剂(过氧化苯甲酰,BPO)用量和HA的质量分数对复合材料弯曲强度和弯曲模量的影响。
6) Bending Modulus
弯曲模量
1.
In order to develop the application of FAST testing system in the area of testing,evaluating,and predicting wool fabrics′ overfeeding sewing-shrinkage,The theory model was found between the ratio of fabric sewing-shrinkage,the ratio of fabrics′ bending modulus to stretching modulus(modulus ratio of bending and stretching),and fabric overfeeding capacity and other physical items.
为开发FAST客观测试仪在测试、评价、预测毛面料超喂缝制下缝缩率等有关方面的应用,建立了面料超喂缝纫时缝缩率与织物弯拉模量比(弯曲模量与拉伸弹性系数之比)、超喂量物理指标之间的理论方程,在分析面料弯拉模量比与FAST测试指标之间关系的基础上,推导了利用FAST测试弯拉模量比的计算方法。
补充资料：表观弹性模量
分子式：
CAS号：
性质： 在减震橡胶制品中，由于橡胶与金属黏着界面的形状效应，不能仅由形状尺寸和橡胶的弹性模量来决定不同方向的弹簧常数，为此将表观弹性模量Eap定义为：圆柱形：Eap=(3+4.9355S2)G正方形：Eap=(3+6.580S2)G无限长柱：Eap=(4+3.290S2)G式中G为剪切弹性模量，S为形状因子。
CAS号：
性质： 在减震橡胶制品中，由于橡胶与金属黏着界面的形状效应，不能仅由形状尺寸和橡胶的弹性模量来决定不同方向的弹簧常数，为此将表观弹性模量Eap定义为：圆柱形：Eap=(3+4.9355S2)G正方形：Eap=(3+6.580S2)G无限长柱：Eap=(4+3.290S2)G式中G为剪切弹性模量，S为形状因子。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。