1) dip slide
浸渍滑板法
2) sol-dipping template method
溶胶-浸渍模板法
3) impregnation method
浸渍法
1.
The mesoporous silicas were impregnated by vion solution and calcined in air at 400 °C,the investigation indicated not only vanadium in samples prepared by impregnation method was incorporated into the famework of mesoporous silicas,but also some dispersed spontaneously onto the surface of mesoporous silicas,and formed a monolayer if total amount of V2O5 increased.
采用X射线衍射技术(XRD)考察了金属氧化物V2O5在介孔二氧化硅分子筛上的分散,研究结果表明应用浸渍法将V2O5浸渍于介孔二氧化硅分子筛中,在低于V2O5熔点的适当温度下焙烧后,与未浸渍V2O5样品相比,晶胞参数a值明显增大,说明钒离子掺入了介孔二氧化硅分子筛的骨架中;在一定范围内随着V2O5加入量的增加其在介孔二氧化硅的表面的分散量也在增加,而V2O5残余晶相量远远低于加入的量,说明V2O5掺入介孔二氧化硅分子筛骨架的同时可在介孔二氧化硅的表面成单层分散。
2.
Silica-supported H_3PW_ 12 O_ 40 catalysts were prepared by the impregnation method, sol-gel technique, and sol-gel technique using ionic liquids as the template, respectively, to solve the problems of H_3PW_ 12 O_ 40 such as low surface area, difficult separation, and reuse.
针对H3PW12O40(HPW)的比表面积小和不易回收利用等缺点,分别采用浸渍法、溶胶-凝胶法和以离子液体为模板剂的溶胶-凝胶法制备了HPW/SiO2催化剂,采用傅里叶变换红外光谱、X射线衍射、N2物理吸附和吸附氨的程序升温脱附等技术对催化剂样品进行了表征,并考察了其对苯硝化反应的催化性能。
3.
Eu-doped TiO2 samples were prepared by the sol-gel method,and further doping which uses ammonia as nitrogen source were carried out by the impregnation method.
本文采用溶胶-凝胶法制备了Eu的TiO2粉体,然后以NH3为N源,采用浸渍法进一步对其处理,获得了同时掺杂Eu、N的纳米TiO2。
4) dipping
[英][dip] [美][dɪp]
浸渍法
1.
This experiment studied the influence of sorption by the concentration, the time of dipping and the time of adsorption.
用浸渍法将活性Al2O3、13A分子筛及活性炭制成负载铜离子的负载型吸附剂来吸附煤油中的硫醇类硫。
2.
The sol-gel dipping method has been used to manufacture TiO2-SiO2 multilayer.
报道了用浸渍法制备的ＴｉＯ２－ＳｉＯ２选择透过膜和这种薄膜与Ｆｅ２Ｏ３－Ｃｒ２Ｏ３－ＭｎＯ２选择吸收涂层的复合徐层。
5) Dipping method
浸渍法
1.
Silver and praseodymium co-doped titanium oxide[(Ag,Pr)/TiO2]nanometer materials were prepared by the dipping method using Pr(NO3)3.
5H2O]、硝酸银(AgNO3)为掺杂的前驱物,纳米二氧化钛(TiO2)为载体,用表面浸渍法制备了(银,镨)/氧化钛[(Ag,Pr)/TiO2]纳米材料。
2.
Using fiber glass cloth as the carrier,the titania photo-catalyst coated on fiber glass cloth was prepared by the dipping method and the adhesive method.
以玻璃纤维布为载体,分别用浸渍法和黏结剂法制备了负载型TiO2光催化剂,用SEM观察了2种方法中TiO2在玻璃纤维表面的负载情况。
补充资料：固体物料浸渍法
分子式：
CAS号：
性质：采用熔融金属、液态润滑剂或其他液态非金属物质来浸渍多孔骨架状固体的方法。该法基于毛细管渗透原理。可分为全浸法，部分浸入法，表面接触法等。还可采用液压，离心力，抽真空等措施增加渗透的附加压力。这种工艺已被广泛应用于许多领域。如多晶氧化铝自润滑含油轴承(将烧好的多晶轴承浸入油中)、金属陶瓷无油润滑活塞环(金属陶瓷浸渍于液态塑料中)、钨渗铜的喷管材料、用熔融的镍、钴、铁浸渍的钨与碳化钛工具和模具材料等。
CAS号：
性质：采用熔融金属、液态润滑剂或其他液态非金属物质来浸渍多孔骨架状固体的方法。该法基于毛细管渗透原理。可分为全浸法，部分浸入法，表面接触法等。还可采用液压，离心力，抽真空等措施增加渗透的附加压力。这种工艺已被广泛应用于许多领域。如多晶氧化铝自润滑含油轴承(将烧好的多晶轴承浸入油中)、金属陶瓷无油润滑活塞环(金属陶瓷浸渍于液态塑料中)、钨渗铜的喷管材料、用熔融的镍、钴、铁浸渍的钨与碳化钛工具和模具材料等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。