1) diamond exposure
金刚石出刃高度
2) maximum protrusion height of diamond
金刚石最大出刃高度
1.
The density, hardness, bending strength and maximum protrusion height of diamond of samples prepared by various sintering methods were compared to that of samples prepared by standard sintering process.
通过对不同热压工艺与传统热压工艺制造出的试块的密度、硬度、抗弯强度及金刚石最大出刃高度对比及用不同热压工艺制造的锯片锯切混凝土、花岗岩板试验的研究表明:对于本试验胎体材料,用低温、高压热压工艺的金刚石最大出刃高度比用传统热压工艺的高;低温、高压热压工艺制造出来的金刚石锯片的性能不比用传统热压工艺制造出来的锯片的性能差;其烧结温度可降低50～110℃,这将能充分发挥金属材料抗氧化性强,低温强度高的优势,从而使金属材料能应用于制作金刚石制品的热压模具。
3) diamond exposure
金刚石出刃
1.
By changing weakly-bonded materials and adding strengthened granular graphite to bit matrix,the diamond exposure of bit was improved.
针对坚硬致密岩石钻进中遇到的钻头打滑、钻进效率低的问题,通过改变弱包镶材料,加入强化的石墨颗粒,进行试验与研究,获得了颗粒状石墨能提高金刚石出刃的初步效果。
4) grinding of diamond
金刚石刃磨
1.
In this paper,a residual stress on cemented carbide inserts caused by grinding of diamond and electrical grinding of diamond,and its effect on cemented carbide strength are studied.
研究了在金刚石刃磨和电金刚石刃磨时硬质合金刀片上引起的残余应力 ,及其对硬质合金强度的影
5) gauge diamond
侧刃金刚石
补充资料：水轮机吸出高度
水轮机吸出高度
static suction of turbine
sht]一I日r、J一x一ellLJg口。门LJ水轮机吸出高度(Static Suetion of turbine)反击式水轮机转轮内压力最低点相对于下游水面的高度，用H.表示，单位为m。反击式水轮机转轮叶片背面接近出水边处的压力最低，是空化的早发区，为避免空化的不利影响，需选用适当的H.来限制该处的真空值。然而水轮机转轮内压力最低点的准确位置很难确定，实践中规定水轮机吸出高度为水轮机空化基准面与尾水位的高差。不同型式的水轮机空化基准面为:立轴泥流式水抢机是导叶下端面(或底环上平面);立轴抽流式水轮机取转轮叶片旋转轴线所在的平面;立轴斜流式取转轮叶片旋转轴线与转轮室内表面交点的所在平面;卧式反击型水轮机是转轮叶片最高点所在的平面。吸出高度一般用下式计算:H.镇10一兰900一K，气Hr式中:Z为电站厂房位!的地面海拔高程，m;K。为裕量系数，‘为模型空化系数;Hr为水轮机额定水头，m。 水轮机安装高程根据水轮机吸出高度确定。反击式水轮机安装高程(Z。)是水轮机叶中心线或轴线的海拔高程，计算及表示如图。 ┌─────┬───┐┌───┐ │:了，书店 │酬万才││自! │ │ │ │├───┼─┼─────┴───┘│队斌F │ │ └───┴─┘ ┌───┬──────┬─────────┐│ │芝二 │劫瞎)%──┬───┤├───┤ z广丁 │ │「_’ │ ││ha! │ │ │ │ │├───┼──────┼─┼───┼───┤│丝上* │ ‘气. │随│巨 │二”. ││ │Z仓 ├─┴───┴───┤│ │ │l │└───┴──────┴─────────┘ 反击式水轮机安装高程示意图(a)立式轴流式水轮机21一Zt十从十尤口; .、___、.、.…_____b。(b)立式混流式水轮机21=Z。+H，+等; 一、，一，一”一’一’一、’一’2 ‘、、。，~~.，，D、C夕砂入2卜柑祖L乙s=乙，一打a一气， ‘Zi一水轮机安装商程;乙一下游水面高程;X一系数(、0.41);D一转轮公称直径;b0一导叶高度