1) chilling period
急冷时间
2) time-controlled sudden cooling
控时急冷
1.
Hot working dies of H13 steel vacuum quenched by the use of the time-controlled sudden cooling tech- nology will obtain fine martensite.
采用真空控时急冷技术对H13钢热作模具进行淬火,可使之得到细小的马氏体组织,从而显著提高热作模具的冲击韧度。
3) emergency time
应急时间
1.
Based on this,algorithms that consider the earliest emergency time and the least relief points with the pulse need are proposed,respectively,which is.
首先,将脉冲消耗应急问题的研究范围限定为各出救点可用资源完全能够满足应急资源脉冲需求的调度问题,从理论上证明了已有的应急资源满足调度需求的充要条件,并进一步给出了应急时间最早的资源调度方案。
4) cooling time
冷却时间
1.
Analysis of Affecting Factor on Cooling Time of Injection Molding;
影响注射成型冷却时间的因素分析
2.
Cooling Time Oetermination of injection Molded Parts;
注塑制品冷却时间的确定
3.
Influence of cooling time on the bond strength of VITA TITANKERAMIK to the cast titanium;
冷却时间对VITA TITANKERAMIC与钛铸件结合强度的影响
5) air cooling time
空冷时间
6) freezing time
冷冻时间
1.
Prediction of freezing time of water-richened aluminum hydroxide sludge;
富水氢氧化铝污泥冷冻时间的预测
补充资料：耐急冷急热性
分子式：
CAS号：
性质：又称耐急冷急热性，耐热崩裂性，耐热冲击性。耐火材料抵抗温度的急变而不破坏的性能叫耐热震性。当制品突然受热（或受冷）发生膨胀（或收缩）时，由于其各部分的变形互相受到制约而产生热应力。当这种热应力超过制品内部的结合力时，制品就产生崩裂或剥落而破坏。耐火制品的耐热震性以实验方法测定。制品的耐热震性除受传递条件影响外主要取决于其热膨胀性、导热性、断裂韧性等，同时也与其组织结构、形状和尺寸等有关。为了防止耐火材料在使用时，因温度急变而引起崩裂，要求耐火材料具有良好的耐热震性。
CAS号：
性质：又称耐急冷急热性，耐热崩裂性，耐热冲击性。耐火材料抵抗温度的急变而不破坏的性能叫耐热震性。当制品突然受热（或受冷）发生膨胀（或收缩）时，由于其各部分的变形互相受到制约而产生热应力。当这种热应力超过制品内部的结合力时，制品就产生崩裂或剥落而破坏。耐火制品的耐热震性以实验方法测定。制品的耐热震性除受传递条件影响外主要取决于其热膨胀性、导热性、断裂韧性等，同时也与其组织结构、形状和尺寸等有关。为了防止耐火材料在使用时，因温度急变而引起崩裂，要求耐火材料具有良好的耐热震性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。