1) bone super,bone super phosphate
骨粉过硫酸钙
2) bone superphosphate
骨粉过磷酸钙
3) calcium chondroitin sulfate
硫酸软骨素钙
1.
A method for preparing calcium chondroitin sulfate from sodium chondroitin was given.
对以硫酸软骨素钠为原料制备硫酸软骨素钙的方法进行了研究,硫酸软骨素钠经水溶解阳离子交换树脂处理,用氢氧化钙和氯化钙离子转型,然后加95%酒精沉淀,制得硫酸软骨素钙;制得白色粉末状产品,收率95。
2.
In this paper,preparation of calcium chondroitin sulfate from sodium chondroitin was completed by a simple optimized process including obtaining of chondroitin sulfuric acids by ion exchange,preparation of calcium chondroitin sulfate by the reaction of chondroitin sulfuric acids and calcium chloride,and alcohol precipitation.
本研究以硫酸软骨素钠为原料 ,将其溶液进行离子交换 ,生成硫酸软骨素酸 ,然后用氯化钙溶液洗脱 ,无水乙醇沉淀 ,即生成硫酸软骨素钙 ,同时对其各项指标进行了检测 ,并通过正交试验优化了工艺条
4) Calcium sulfate cement
硫酸钙骨水泥
1.
Experimental research on biomechanics of calcium sulfate cement in thoracolumbar burst fractures;
胸腰椎爆裂骨折模型中硫酸钙骨水泥椎体成形术的生物力学性能
2.
Experimental research on biomechanics of calcium sulfate cement in thoracolumbar burst fractures
硫酸钙骨水泥在胸腰椎爆裂骨折椎体成形术中的生物力学性能
5) calcium sulfate cement(CSC)
硫酸钙骨水泥(CSC)
6) calcium sulfate and freeze-dried bone
硫酸钙/冻干骨
1.
Objective: To investigate the influence on the hydrophobicity and compatibility of bioactive porous scaffold composed of calcium sulfate and freeze-dried bone, which is modified with collagen typeⅠ.
背景:前期研究已经成功制备了硫酸钙/冻干骨复合型生物多孔支架,但其表面的疏水性不利于细胞黏附、增殖。
补充资料：过氧化单硫酸钾与硫酸二钾和硫酸氢钾的化合物
CAS：37222-66-5
中文名称：过氧化单硫酸钾与硫酸二钾和硫酸氢钾的化合物
英文名称：Peroxymonosulfuric acid, monopotassium salt, mixture with dipotassium sulfate and potassium hydrogen sulfate； potassium peroxymonosulfate sulfate,(2khso5.khso4.k2so4)； Peroxymonosulfuric acid,monopotassium salt,mixture with dipotassium sulfate and potassium hydrogen sulfate
中文名称：过氧化单硫酸钾与硫酸二钾和硫酸氢钾的化合物
英文名称：Peroxymonosulfuric acid, monopotassium salt, mixture with dipotassium sulfate and potassium hydrogen sulfate； potassium peroxymonosulfate sulfate,(2khso5.khso4.k2so4)； Peroxymonosulfuric acid,monopotassium salt,mixture with dipotassium sulfate and potassium hydrogen sulfate
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条