1.
on the rate of the first class products of metallic chromium with metallothermic process and points out effective measures to increase the rate of the first class products.
阐述了炉外法金属铬冶炼中氧化铬和还原剂的成分及粒度、发热剂选取、发热量控制、加料速度等因素对一级品率的影响 ,指出了提高一级品率的有效途径。
2.
The data of metallic chromium between export commdity examination and producing examination are analysed contrastively.
对出口金属铬的商检结果与生产检验结果进行了对比分析。
3.
The Electrodeposition process of metallic chromium from chromic acid solution was investigated with the techniques of electrochemical impedance spectroscopy (EIS), polarization curves.
采用电化学阻抗、阴极极化曲线等测试技术，考察了铬酸溶液中金属铬的电沉积过程实验证实了镀铝阴极过程中表面吸附膜的存在，它改变了阴极表面的状态，导致阴极极化曲线上出现电流峰，迫使阴极电位负移，为金属铬的电沉积创造了条件电化学阻抗测量发现，在Ｎｙｑｌｌｉｓｔ图上出现上一个代表吸附膜的“感抗圈”。
6) metal chrome
金属铬
1.
Abstact The waste source of metal chrome prod uction are expounded,the method and results are discussed according to the practice.
阐述了金属铬生产中“三废”的来源,结合实际论述了三废治理的办法和效果。
2.
In the experiment,the ITHAC-2002 was used to determine H_2 in metal chrome,Op-tions of analysis current,analysis time,degassing current,degassing time and gradient time were made one by one.
通过试验，实现了ＩＴＨＡＣ－２００２仪对金属铬中氢的测定。
补充资料：金属化纸和金属化薄膜
表面上蒸镀一层很薄 (0.1微米左右)的金属层的纸或薄膜。金属化纸曾应用于电缆、变压器作为屏蔽层,现多用于制造电容器。金属化纸和金属化薄膜的特点是具有自愈性,即当某处击穿时,短路电流使击穿部位周围的金属膜熔化并蒸发而又恢复绝缘性能，因此显著减少纸或薄膜中贯穿性导电疵点和弱点对击穿强度的影响，从而提高工作场强。低压纸介电容器如用铝箔极板（6～7微米）,必须用2～3层纸或薄膜,若用金属化纸或金属化薄膜,只要1层即可,极板的厚度也由6～7微米减少到0.1微米左右，大大节省材料。直流或脉冲电容器用金属化纸时，为了提高绝缘电阻，可以在纸的单面或双面涂以约1微米厚的快干纤维漆，然后在真空中蒸镀0.1微米的金属膜。交流电容器用的金属化纸或金属化薄膜，为了不使介质损耗增大，不喷漆，而是在纸或薄膜表面上直接蒸镀金属膜。用于蒸镀金属膜的金属有锌、镉、镍和铝等，以锌最适合（沸点较低）。有些薄膜（例如聚酯薄膜）可以先在表面上蒸镀银层，然后再蒸镀锌层。
金属化纸或金属化薄膜吸潮后，特别是在较高温度下容易被损伤腐蚀，在储存、加工过程中要采取适当的防潮措施。金属化纸一般不可用氯化物浸渍，以防止纸中析出的氢同氯化物浸渍剂析出的氯作用形成腐蚀性的氯化氢；但加了某些特殊的稳定剂后也可以用氯化物浸渍。
金属化纸或金属化薄膜吸潮后，特别是在较高温度下容易被损伤腐蚀，在储存、加工过程中要采取适当的防潮措施。金属化纸一般不可用氯化物浸渍，以防止纸中析出的氢同氯化物浸渍剂析出的氯作用形成腐蚀性的氯化氢；但加了某些特殊的稳定剂后也可以用氯化物浸渍。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条