1) zone melting with focused radiation
辐射聚焦的区域熔炼
2) joule heat zone melting
焦耳热区域熔炼<冶>
3) Zone melting
区域熔炼
1.
high purity indium was prepared by the method of a combination of electrolytic refining and zone melting.
采用电解精炼 区域熔炼法 ,获得了 99 9999%高纯铟。
2.
The methods of preparing high purity iron include solvent extraction,ion exchange,electrolytic refining,zone melting,and so on.
本文介绍了溶剂萃取、离子交换、电解精炼和区域熔炼等冶金提纯方法在高纯铁制备过程中的应用。
4) zone-melting
区域熔炼
1.
The zone-melting temperature of YBaCuO tapes were decreased under 945□ by doping Ag and PbO in YBaCuO films, which made zone-melting process possible with Ag substrate not melted.
通过掺杂Ag和PbO的方法降低YBaCuO的区熔温度到945℃以下,从而能够在金属Ag基底上进行区域熔炼,获得有织构的超导带材。
5) Regional Smelt
区域熔炼
1.
Making the Metal in High Solidification by the Way of Regional Smelt;
区域熔炼法制备高纯度金属
2.
Method of regional smelt has been adopted in the electronic industrial production.
在电子工业生产中采用区域熔炼的方法,能将金属的纯度提高到99。
6) zone-refining by solar rediation zone-refining
太阳能辐射区域精炼<冶>
补充资料:区域熔炼
指根据液体混合物在冷凝结晶过程中组分重新分布(称为偏析)的原理,通过多次熔融和凝固,制备高纯度的(可达99.999%)金属、半导体材料和有机化合物的一种提纯方法,属于热质传递过程。此法是由W.G.范在1952年提出的,最初应用于高纯度锗的生产。
区域熔炼的典型方法是将被提纯的材料制成长度为0.5~3m(或更长些)的细棒,通过高频感应加热,使一小段固体熔融成液态,熔融区液相温度仅比固体材料的熔点高几度,稍加冷却就会析出固相。熔融区沿轴向缓慢移动(每小时几至十几厘米)。杂质的存在一般会降低纯物质的熔点,所以熔融区内含有杂质的部分较难凝固,而纯度较高的部分较易凝固,因而析出固相的纯度高于液相。随着熔融区向前移动,杂质也随着移动,最后富集于棒的一端,予以切除。一次区域熔炼往往不能满足所要求的纯度,通常须经多次重复操作,或在一次操作中沿细棒的长度依次形成几个熔融区。
区域熔炼设备简单,产品纯度高,操作可以自动化,但生产效率低。目前,已经用于制备铝、镓、锑、铜、铁、银等高纯金属材料。
区域熔炼的典型方法是将被提纯的材料制成长度为0.5~3m(或更长些)的细棒,通过高频感应加热,使一小段固体熔融成液态,熔融区液相温度仅比固体材料的熔点高几度,稍加冷却就会析出固相。熔融区沿轴向缓慢移动(每小时几至十几厘米)。杂质的存在一般会降低纯物质的熔点,所以熔融区内含有杂质的部分较难凝固,而纯度较高的部分较易凝固,因而析出固相的纯度高于液相。随着熔融区向前移动,杂质也随着移动,最后富集于棒的一端,予以切除。一次区域熔炼往往不能满足所要求的纯度,通常须经多次重复操作,或在一次操作中沿细棒的长度依次形成几个熔融区。
区域熔炼设备简单,产品纯度高,操作可以自动化,但生产效率低。目前,已经用于制备铝、镓、锑、铜、铁、银等高纯金属材料。