1) twin-heat
二炉连浇
2) continuous casting heats
连浇炉数
1.
The problem of increasing the continuous casting heats of tundish and decreasing the uses of metal band is dealt with for the purpose of redusing cost.
针对尽量提高中间包的连浇炉数,同时降低插铁板的数量,减少连铸生产成本的问题,结合宝钢一连铸实际生产的钢种情况和不同钢种对中间包的使用要求,从生产组织角度上建立了中间包连浇炉数和插铁板次数之间的理论计算关系,得出了在不同生产钢种条件下可以达到的最佳中间包连浇炉数和最佳的插铁板次数,并就插铁板对连浇炉数的影响进行了分析,同时将理论计算和实际结果进行了对比验证,就实际生产组织存在的差距进行了分析。
2.
The continuous casting heats increase to 48 heats from 16 and the molten recovery to 97.
中间包快换技术大大提高了铸机作业率,连浇炉数由快换前的16炉提高到48炉以上,钢水收得率由97。
3.
The continuous casting heats of tundish have been uninterruptedly rising by taking a series technical measures such as rational use of refractory material and improvement in the smelting process.
武钢第一炼钢厂通过合理使用耐材、改善冶炼工艺等措施 ,使中间包连浇炉数不断提高。
3) sequence continuous casting
多炉连浇
1.
The essence of sequence continuous casting in EAF steel plant is the joining and matching of multiprocess of production and the key is to shorten tap to tap time on EAF.
全连铸电炉炼钢厂的多炉连浇问题实质是多工序的衔接匹配问题。
4) non oxidation continuous continuous casting
无氧化多炉连浇
5) continuous pouring top furnace
炉顶连续浇注
6) united casting
连浇
1.
Owing to the perniciousness of crack occuring in gate pier and bottom plate separate bin casting,the paper analysed the causes of crack and proposed the gate pier and bottom plate united casting plan.
针对闸墩与底板分仓浇筑易出现裂缝的危害,分析了裂缝成因机理,并提出了闸墩与底板连浇的方案。
补充资料：多炉连浇
多炉连浇
sequence casting
duolu}ianjioo多炉连浇(sequenee casting)指在连续铸钢过程中上一次引锭杆可连浇数炉钢水的操作。据统计，5炉连浇与单炉浇铸相比，铸坯产量提高约50%，金属收得率提高约3%，操作费用降低约25%，因此多炉连浇炉数代表了连铸机生产水平。多炉连浇是一项高难技术。它是连铸设备、工艺、管理水平的综合体现。为实现多炉连浇，已开发了一系列技术:(1)采用钢包回转台(见钢包支承装置)，实现快速更换钢包(能在1一Zmin完成)。(z)采用大容量中间罐，保证为更换钢包不降低拉速提供充足时间。(3)结晶器在线调宽技术。过去改变钢种和浇注断面必须中断浇注。采用结晶器在线调宽和异钢种连续浇铸技术，可使连浇时间大大延长。据统计，结晶器采用在线调宽，平均连浇9.7炉，而不使用在线调宽仅为5.5炉。(4)快速更换中间罐和更换浸入式水口技术。(5)防止水口堵塞技术。(6)减少连铸机的漏钢事故。由于多炉连浇有明显的经济效益，各类连铸机多炉连浇水平有明显提高。多炉连浇记录不断涌现。如1991年日本水岛厂板坯连铸机连浇927炉(300tLD炉)、34天、一次连浇坯24.8万t。4流方坯连铸机连浇1015炉、38天、一次连浇坯15万t以上。 (马怡绅张永霖)