1) dilute uranium alloy
低合金铀
2) uranium-niobium alloy
铀铌合金
1.
Computer simulation and experimental investigation on casting grain size for uranium-niobium alloy;
铀铌合金铸造晶粒度的计算机模拟与实验研究
2.
The results show that preheating and annealing can shorten the incubation period for the reactions of bulk uranium and uranium-niobium alloys with H_2.
用压力 体积 温度(P V T)法研究了铀和铀铌合金与氢气反应的动力学过程。
3.
The surface reaction of uranium-niobium alloy with carbon monoxide has been studied by x-ray photoelectron spectroscopy(XPS) and gas chromatography(GC).
采用X射线光电子能谱 (XPS)和气相色谱 (GC)研究了铀铌合金在 2 5℃与CO反应后表面层的组成和反应气氛的变化 。
3) uranium niobium alloy
铀铌合金
1.
Electrochemical studies are performed to investigate the corrosion resistance of uranium niobium alloy before and after passivated with carbon monoxide.
采用电化学方法研究了铀铌合金经CO( 0 3MPa)钝化前后的电化学耐蚀性能 ,并用X射线光电子能谱 (XPS)分析了铀铌合金经CO钝化后表面层的组成。
4) depleted uranium alloys
贫铀合金
1.
The atmospheric corrosion characteristic of depleted uranium alloys in environments of indoor and outdoors of marine and inland environment was studied.
通过对贫铀合金在沿海、内地的户外暴露试验和库内露置试验,研究并得到了贫铀合金的大气腐蚀特性,分析了大气中SO2、Cl-及相对湿度腐蚀贫铀合金的原因与结果。
5) uranium alloy
铀合金
1.
75Ti uranium alloy that chronically exposed and stored in the typical atmosphere is summarized in this paper.
概述了U - 0 75Ti铀合金在典型大气环境中长期曝露和贮存时的腐蚀行为及应力腐蚀敏感性研究的一些主要结果 ,得到了铀合金在长期贮存条件下 ,能够长期保持极低的腐蚀速率和不存在明显的大气应力腐蚀的重要规律 。
6) U-Ti alloy
铀-钛合金
1.
Effect of carbon content on tensile property of U-Ti alloys at elevated temperature;
铀-钛合金高温拉伸性能研究
补充资料：低加浓铀
分子式：
CAS号：
性质：铀中含有0.71％<235U<5％(质量)为低加浓铀。轻水堆中使用的铀燃料含235U的浓缩度约在2％～4％(质量)，属低加浓铀。通过耗费大量电力的同位素分离工艺获得。
CAS号：
性质：铀中含有0.71％<235U<5％(质量)为低加浓铀。轻水堆中使用的铀燃料含235U的浓缩度约在2％～4％(质量)，属低加浓铀。通过耗费大量电力的同位素分离工艺获得。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。