1) isostatic preform
等静压预形坯
2) isopressed compact
等静压坯
3) preform
[英][pri:'fɔ:m] [美][pri'fɔrm]
预成形坯
1.
The design of preform and forging die is analyzed with the precautions and problems often observed during hog-forging.
本文以冲击块为例介绍了粉末冶金热锻的工艺,对热锻中的预成形坯设计、锻模设计作了进一步探讨,分析了热锻中的注意事项和经常出现的问题。
2.
SiCp and binder were mixed together and SiCp preforms were prepared by warm pressing, thermaldebinding and pre-sintering.
在本实验中将SiC颗粒与粘结剂混合,温压制备成坯块,进行了热脱脂与预烧结,研究了热脱脂一预烧结后坯块的线性膨胀率、孔隙度、强度与工艺条件的关系,对预成形坯的显微组织形貌进行分析。
4) Precompression of plywood base
板坯预压
5) preformed compact
预压坯
6) cold isostatic pressing
冷等静压成形
1.
The effects of dry pressing with cold isostatic pressing under different pressure on the structure and properties of the green and sintered body of ceramics was studied.
本文通过研究在不同压力下进行干压结合冷等静压成形过程对陶瓷素坯体和烧结体的结构、性能的影响,得出了最佳的成形工艺条件,即干压压力为20T、冷等静压压力为200MPa。
2.
A concise review was made for the development status of cold isostatic pressing technique.
简要概述了冷等静压成形技术的发展及现状,着重介绍了这种成形方法的特点及工艺技术要求,以及在精细陶瓷成形方面的应用结果。
补充资料:爆炸等静压成型
分子式:
CAS号:
性质:利用炸药的爆炸,产生高压冲击波传给液体介质,加压于模体,使粉料在各方向同时均匀受压。与一般等静压成型的区别在于:装置简单,不带附属的高压系统,爆炸的瞬间可达30000~100000MPa的巨大高压,操作周期短,成形后坯体密度高,硬度大,可再精加工。操作控制较难,要加强防护和安全。
CAS号:
性质:利用炸药的爆炸,产生高压冲击波传给液体介质,加压于模体,使粉料在各方向同时均匀受压。与一般等静压成型的区别在于:装置简单,不带附属的高压系统,爆炸的瞬间可达30000~100000MPa的巨大高压,操作周期短,成形后坯体密度高,硬度大,可再精加工。操作控制较难,要加强防护和安全。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条