1)  residual hardness
残留硬度
2)  residual hardness
残余硬度,残留硬度
3)  residual hardness of water
水的残留硬度
4)  hardness leakage
(给水)残留硬度
5)  hard residue
硬性残留物
6)  residual strength
残留强度
1.
The results show that the residual strength of the three kinds of materials declines with increasing the thermal shock temperature,and the critical temperatures for sharply decline of residual strength are 410,370 and 330.
结果表明,3组金属陶瓷试样的热震残留强度均随热震温度的升高而降低,其热震残留强度急剧下降的临界温度分别为410、370和330℃。
2.
The influence of increasing sodium silicate addition and adding organic ester on residual strength and final strength after 24 h of sodium silicate sand was analyzed with orthogonal experiments.
通过正交试验分析了水玻璃的加入量增加和有机酯的加入对水玻璃砂的残留强度和24 h终强度的影响程度大小,结果表明:有机酯的加入使水玻璃砂的24 h终强度达到了普通水玻璃砂的要求;水玻璃加入量的减少,使有机酯硬化水玻璃砂的溃散性有较大提高。
3.
The influences of furnace-cooling and air-cooling on residual strength values of sodium silicate sand after heating at high temperature was compared by experiment.
通过实验对比了炉冷和空冷两种冷却方式对水玻璃砂经高温加热后的残留强度值测定的影响,认为炉冷的方式更接近于铸型实际的冷却情况,得到的结果能更好的评价溃散剂真实的溃散效果。
补充资料:工程塑料硬度的检测--巴氏硬度计
HBa-1巴 氏 硬 度 计巴柯尔 (Barcol) 硬度 ( 简称巴氏硬度 ) 最早由美国 Barber-Colman 公司提出,是近代国际上广泛采用的一种硬度门 类,以特定压头在标准弹簧的压力作用下压入试样,以压痕的深浅表征试样的硬度。巴柯尔硬度计(巴氏硬度计)作为 专门测量玻璃钢制品、增强或非增强硬塑料、铝及铝合金、黄铜、紫铜等较软金属硬度的专用检测工具 ( 特别 适用于玻璃钢制品 ),已被大多数国家或国际组织认可。美国材料试验协会( ASTM )、日本工业规范( JIS )、中国等国家相继制定 《用巴柯尔硬度计测量玻璃钢( GRP )硬度试验方法》,《纤维增强塑料巴氏(巴柯尔)硬度试验方法》GB/T3854-1983 的国家标准。因此,巴柯尔硬度计是各生产单位、计量部门在质量认证、质量监控、计量测试等方面首选的专用检测仪器。 无锡市计量科学研究所,是我国制定巴柯尔硬度检定标准的主要参与者、巴柯尔硬度最高标准器的拥有者和国产第一台巴柯尔硬度计的研制和生产单位,也是国家实验室认证的巴柯尔硬度计专业检测机构。经过二十多年的不断完善,本所生产的 H Ba 系列巴柯尔硬度计的各项性能和技术指标完全与美国 Barber-colman 公司 GYZJ 系列硬度计相媲美 。