Hot rolled ribbon steel for container at Lai Steel is a newly developed steel type,and in this paper,the problems of longitudinal spilt,sticking breakout and the cold-bended split caused by endogenous inclusions,which are formed in continuous casting process,are analysed,and then measures have been taken,at last the quality defects are under control step by step,and satisfy the production demand.
莱钢热轧窄带集装箱钢是新开发耐候钢种,本文针对集装箱钢连铸生产中出现的纵裂、粘连漏钢及铸坯内部夹杂物造成的冷弯裂纹问题,通过分析原因,采取措施,逐步控制质量缺陷,达到生产要求。
4) wooden case for glass packing
玻璃包装木箱
5) container sheet steel
集装箱板钢
1.
There are problems of low drawing heat quantity and its instability in mold for thin slab casting of container sheet steel.
针对集装箱板钢薄板坯连铸过程中拔热量偏低及不稳定问题,根据集装箱板钢种及相适应的结晶器保护渣特点,分析了结晶器拔热量与保护渣理化性能的关系,提出了相应的保护渣理化性能指标。
6) container steel
集装箱用钢
1.
Experimental studies are made with Gleeble-1500 thermal simulator on the metallic plastic deformation resistance of container steel,involving actual measurements of the deformation resistances of the said steel under different deformation temperatures,deformation rates and deformation severities,and analysis of the influences by different process parameters on the deformation resistance.
利用Gleeble-1500热模拟试验机对集装箱用钢金属塑性变形抗力进行试验研究。
2.
The dynamics curve of continuous cooling transformation of 700 MPa container steel has been determined by means of Gleeble-3800 thermo-simulation experiment machine.
通过Gleeble-3800热模拟试验机测定了700 MPa级集装箱用钢的连续冷却转变动力学曲线(CCT曲线);研究了在不同温度下进行压缩变形、以及变形后冷却到不同的温度区间保温,变形温度和保温温度对钢的组织形态和性能的影响,为生产实践和新工艺的制定提供了参考依据。
3.
The influence of holding and deforming temperatures on the microstructure and hardness of 700 MPa container steel is investigated by Gleeble-3800 thermal simulator and optical microscope.
采用G leeb le-3800热模拟实验机,结合光学显微镜,研究了保温温度及变形温度对700 MPa级集装箱用钢组织和硬度的影响。
补充资料：玻璃纤维增强聚甲基丙烯酸甲酯透明玻璃钢
分子式：
CAS号：
性质： 玻璃纤维增强的有机玻璃。具有好的机械强度，冲击强度可比普通有机玻璃高5～10倍，半透明、耐光耐候性优良。制法与铸型本体聚合制有机玻璃相似，在模具中每铺一层玻璃纤维，浇一层甲基丙烯酸甲酯预聚浆料，使其充分浸润，最后密封后加热固化脱模。主要用作建筑材料，如遮阳板等。
CAS号：
性质： 玻璃纤维增强的有机玻璃。具有好的机械强度，冲击强度可比普通有机玻璃高5～10倍，半透明、耐光耐候性优良。制法与铸型本体聚合制有机玻璃相似，在模具中每铺一层玻璃纤维，浇一层甲基丙烯酸甲酯预聚浆料，使其充分浸润，最后密封后加热固化脱模。主要用作建筑材料，如遮阳板等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条