1) semifusain
半丝炭
2) semifusinite
['semi'fju:zinait]
半丝炭煤素质<地>
3) Carbon filaments
炭丝
1.
Carbon filaments and hollow carbon balls were found on the surface of troilite balls.
经ＳＥＭ、ＴＥＭ和ＥＤＸ的研究，证实它们是纳米级的炭球和炭丝。
4) fusain
[英][fju:'zein] [美][fju'zen]
丝炭
1.
ESR characteristics of vitrain, fusain and inertiniterich durain have been studied and compared with those of woody tissue, H2SO4-oxidated and carbonized woody tissues and peat, by means of ESR spectrometer and simulation method.
利用顺磁共振技术和模拟试验方法，对镜煤、丝炭和暗煤同木材、氧化木材、炭化木材和氧化草本泥炭的顺磁共振特性进行了对比研究，首次提出了氧化丝炭和暗煤的顺磁共振图谱。
2.
The type and the content of minerals and the structural characteristics of organic matter of the vitrain and the fusain in several coals from four different mine areas were compared by the means of X ray diffraction(XRD).
通过 X射线衍射 ( XRD)分析对 4个不同矿区煤中的镜煤和丝炭中矿物质类型和相对含量、煤中有机质的结构特征进行了对比分析。
5) removing fusinite
丝炭脱除
6) vitrifusain
玻璃丝炭
补充资料：半补强炭黑
C 分子量12．01
无味无嗅黑色粉状松散物。不溶于溶剂。暴露在空气中吸潮。平均粒径60-130nm。比表面积20-35m2／g。真密度1．8g／cm3左右。
生产方法 采用油炉法和气炉法。油炉法是以重油、渣油为原料，配合一定量的空气送入反应炉内，在1100℃左右进行不完全燃烧、裂解，经急冷、收集、造粒而得。气炉法是以天然气为原料，配合一定量的空气通过火嘴箱，同时引入密闭反应炉中，在1250℃左右进行不完全燃烧、裂解，经冷却、收集和造粒而得。
应用 作为填充料，用于天然橡胶和各种合成橡胶(尤其对氯丁橡胶和丁腈橡胶兼具补强和填充作用)，有配量大、分散性好、加工性良好等特点，能使橡胶提高扯断伸长率、弹性和耐老化性，降低永久变形等，从而可用于生产胎体缓冲胶、帘布胶、钢丝包布胶、载重轮胎胎侧胶以及内胎、运输带内层、电缆包胶、胶管、胶鞋等各种橡胶制品。
无味无嗅黑色粉状松散物。不溶于溶剂。暴露在空气中吸潮。平均粒径60-130nm。比表面积20-35m2／g。真密度1．8g／cm3左右。
生产方法 采用油炉法和气炉法。油炉法是以重油、渣油为原料，配合一定量的空气送入反应炉内，在1100℃左右进行不完全燃烧、裂解，经急冷、收集、造粒而得。气炉法是以天然气为原料，配合一定量的空气通过火嘴箱，同时引入密闭反应炉中，在1250℃左右进行不完全燃烧、裂解，经冷却、收集和造粒而得。
应用 作为填充料，用于天然橡胶和各种合成橡胶(尤其对氯丁橡胶和丁腈橡胶兼具补强和填充作用)，有配量大、分散性好、加工性良好等特点，能使橡胶提高扯断伸长率、弹性和耐老化性，降低永久变形等，从而可用于生产胎体缓冲胶、帘布胶、钢丝包布胶、载重轮胎胎侧胶以及内胎、运输带内层、电缆包胶、胶管、胶鞋等各种橡胶制品。