1) cosogenic
[核]宇宙成形的
2) cosmoplastic
[英][,kɔzmə'plæstik] [美][,kɑzmə'plæstɪk]
宇宙形成的
3) cosmogenic
[英][,kɔzmə'dʒenik] [美][,kɑzmə'dʒɛnɪk]
宇宙成因的
4) cosmogenic nuclide
宇宙成因核素
1.
Using in situ produced cosmogenic nuclides 10Be and 26Al we have dated high lacustrine shorelines around the Cuochuolong Lake: The exposure ages are 3.
利用原地生成宇宙成因核素确定了藏南错戳龙的高湖面阶地的形成时间为3。
2.
We have measured average erosion rates, using cosmogenic nuclide 10Be and 26Al dating technique, in northwest and the northern part of Tibet.
利用宇宙成因核素10Be和26Al对西昆仑和可可西里北部地表基岩的剥蚀速率进行了测定,得到的结果是:西昆仑的平均剥蚀速率为12m/Ma,可可西里北部的平均剥蚀速率为15m/Ma。
3.
This paper introduces the formation mechanism of cosmogenic nuclides, the theoretical background of their quantification, and the applications of cosmogenic nuclides in the earth sciences in recent years.
随着加速器质谱的出现 ,宇宙成因核素展示了其在地球科学中的生命力。
6) cosmogenic nuclides
宇宙成因核素
1.
Estimation of exposure time and erosion rate as well as thickness of erosion surface using cosmogenic nuclides ~(10)Be and ~(26)Al;
应用宇宙成因核素~(10)Be和~(26)Al估算剥蚀面的暴露时间及剥蚀速率和剥蚀厚度
2.
The reactions producing cosmogenic nuclides mainly involve spallation,capture of neutrons and muon reaction.
宇宙成因核素地表暴露测年方法,是近年来迅速发展起来的一种新的同位素地质年代学方法。
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。