说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> (加热)热调谐时间
1)  thermal tuning time(heating)
(加热)热调谐时间
2)  thermal tuning time(cooling)
(冷却)热调谐时间
3)  heating time
加热时间
1.
Analysis to the influences of heating time on the Bell-type furnace;
浅析罩式退火炉加热时间的影响因素
2.
The equipment is composed of extrusion,liquid pressure station,intermediate frequency heating system(another introduction),cooling system,electric cabinet,operation bed,kcn-4s/w add-subtract counter can be used as high precise timer to control the tube heating time of the GTR type intermediate frequency respond heating stove expends to the tubes.
设备由挤压主机、液压站、中频加热系统(另外介绍)、冷却系统、电气柜、操作台组成,其中KCN-4S/W加减计数器可以用作高精度的定时器来控制GTR型中频感应加热炉对管子的加热时间。
3.
Researches show that when the air is preheated to 900 ℃ and oxygen concentration is enriched to 54%,the heating time decreases by 38%,the product rate increases by 61%,thermal efficiency increases by 30.
研究表明:在预热900℃和含氧体积分数为54%条件下燃烧与传统燃烧相比,加热时间可缩短38%,生产率可提高61%,热效率可提高30。
4)  glow plug heating time
预热塞加热时间
5)  time cook
加热时间键
6)  Long-time heating
长时间加热
补充资料:金属热处理 :感应加热热处理
        用感应电流使工件局部加热的表面热处理工艺。这种热处理工艺常用於表面淬火﹐也可用於局部退火或回火﹐有时也用於整体淬火和回火。20世纪30年代初﹐美国﹑苏联先后开始应用感应加热方法对零件进行表面淬火。随著工业的发展﹐感应加热热处理技术不断改进﹐应用范围也不断扩大。
         基本原理 将工件放入感应器(线圈)内(图1 感应加热原理 )﹐当感应器中通入一定频率的交变电流时﹐周围即產生交变磁场。交变磁场的电磁感应作用使工件内產生封闭的感应电流──涡流。感应电流在工件截面上的分布很不均匀﹐工件表层电流密度很高﹐向内逐渐减小(图2 沿工件截面的电流密度分布 )﹐这种现象称为集肤效应。工件表层高密度电流的电能转变为热能﹐使表层的温度昇高﹐即实现表面加热。电流频率越高﹐工件表层与内部的电流密度差则越大﹐加热层越薄。在加热层温度超过钢的临界点温度后迅速冷却﹐即可实现表面淬火。
         分类 根据交变电流的频率高低﹐可将感应加热热处理分为超高频﹑高频﹑超音频﹑中频﹑工频 5类。①超高频感应加热热处理所用的电流频率高达27兆赫﹐加热层极薄﹐仅约0.15毫米﹐可用於圆盘锯等形状复杂工件的薄层表面淬火。②高频感应加热热处理所用的电流频率通常为200~300千赫﹐加热层深度为0.5~2毫米﹐可用於齿轮﹑汽缸套﹑凸轮﹑轴等零件的表面淬火。③超音频感应加热热处理所用的电流频率一般为20~30千赫﹐用超音频感应电流对小模数齿轮加热﹐加热层大致沿齿廓分布﹐粹火后使用性能较好。④中频感应加热热处理所用的电流频率一般为2.5~10千赫﹐加热层深度为2~8毫米﹐多用於大模数齿轮﹑直径较大的轴类和冷轧辊等工件的表面淬火。⑤工频感应加热热处理所用的电流频率为50~60赫﹐加热层深度为10~15毫米﹐可用於大型工件的表面淬火。(见彩图 差温炉淬火600毫米直径冷轧辊工频感应加热淬火大型铸钢件的热处理炉真空淬火炉 )