1) maleic anhydride grafted polyolefins
顺酐接枝聚烯烃
2) maleic anhydride grafted polyethylene
顺酐接枝聚乙烯
3) Polyolefin-g-MAH
马来酸酐接枝聚烯烃
1.
Progress in Study of Polyolefin-g-MAH/Nylon Alloy;
马来酸酐接枝聚烯烃／尼龙共混合金的研究进展
4) grafted polyolefin
接枝聚烯烃
5) Graft Polyolefin
聚烯烃接枝物
6) PP-g-MAH
马来酸酐接枝聚丙烯
1.
To improve the interfacial compatibility between wood fiber and polypropylene as well as the toughness of wood fiber-polypropylene composites,maleic anhydride grafted polypropylene(PP-g-MAH) and maleic anhydride grafted styrene-ethylene-butadiene-styrene copolymer(SEBS-g-MAH) were used as modifiers.
为了改善木纤维与聚丙烯之间的界面相容性,提高木塑复合材的刚度和韧性,该文利用马来酸酐接枝聚丙烯(PP-g-MAH)及马来酸酐接枝苯乙烯-乙烯-丁二烯-苯乙烯嵌段共聚物(SEBS-g-MAH)对其进行增强和增韧改性。
2.
PA6/PP alloy was prepared using PP-g-MAH as compatilizer, and the effects of varied content of PP-g-MAH and PA6/PP ratio on alloy properties were studied.
以马来酸酐接枝聚丙烯(PP-g-MAH)为增容剂,制备了PA6/PP合金,研究了PA6/PP配比及PP-g-MAH用量对PA6/PP合金性能的影响。
3.
PP-g-MAH/down powder blend films with different content of powder were obtained after down powder were pretreated by different kinds of plasticizers,and the influence of down powder content,the type of PP,and the kind of plasticizers on the mechanical properties of blend films were studied.
采用不同增塑剂对羽绒粉体处理,制备了不同羽绒含量的马来酸酐接枝聚丙烯(PP-g-MAH)/羽绒粉体共混膜,分析了粉体含量、PP种类及不同增塑剂对共混膜力学性能的影响。
补充资料：顺酐接枝聚烯烃
分子式：
分子量：
CAS号：
性质：各种聚乙烯、聚丙烯、乙烯/乙酸乙烯共聚物与顺丁烯二酸酐接枝共聚所得的一类改性聚烯烃。其中顺酐的含量仅0.1%-0.5%(质量)，但能使聚烯烃的非极性得到改变，从而使聚烯烃具有粘接性、涂饰性、油墨印刷性等。这类改性聚烯烃可提高塑料的机械性能和耐热性。可用作挤塑复合膜的粘接层、钢管被覆层，也可用作聚烯烃与极性聚合物如尼龙等共混时的相容剂等。可在有机过氧化物存在下将熔融的聚烯烃与顺丁烯二酸酐进行接枝共聚而制成。
分子量：
CAS号：
性质：各种聚乙烯、聚丙烯、乙烯/乙酸乙烯共聚物与顺丁烯二酸酐接枝共聚所得的一类改性聚烯烃。其中顺酐的含量仅0.1%-0.5%(质量)，但能使聚烯烃的非极性得到改变，从而使聚烯烃具有粘接性、涂饰性、油墨印刷性等。这类改性聚烯烃可提高塑料的机械性能和耐热性。可用作挤塑复合膜的粘接层、钢管被覆层，也可用作聚烯烃与极性聚合物如尼龙等共混时的相容剂等。可在有机过氧化物存在下将熔融的聚烯烃与顺丁烯二酸酐进行接枝共聚而制成。