1) thermal distorsion temperature
热形变温度
2) HDT
热变形温度
1.
In this paper,several terms of thermal- setting resin are covered in detail, including HDT,Martin Temperature, Tg, insulating grade temperature & anti - corrosion application temperature, which is quite beneficial to resin choice or proper resin application.
通过对热固性树脂的热变形温度、马丁耐热、玻璃化转变温度、绝缘耐热等级以及耐腐蚀使用温度五个温度概念的辨析,帮助人们在使用过程中理清头绪,正确选择树脂,有效应用于实际生产。
2.
The effect of wollastonite on the HDT and mechanical properties of PP,and the effect of LDPE on the HDT and mechanical properties of PP/wollastonite composites were investigated.
将PP与高填充量的硅灰石通过双螺杆挤出机熔融共混制得了PP/硅灰石复合材料;将PP/硅灰石复合材料与LDPE通过双螺杆挤出机进行二次共混制得了PP/LDPE/硅灰石三元复合材料;研究了硅灰石对PP的热变形温度(HDT)和力学性能的影响以及LDPE对PP/硅灰石复合材料HDT和力学性能的影响。
3) Heat Distortion Temperature
热变形温度
1.
Its heat distortion temperature reached to 265 ℃.
利用正交试验优选了树脂配方,该树脂体系在有效降低粘度的同时,还提高了耐热性,优选配方树脂体系的热变形温度达到265℃。
2.
The heat distortion temperature and notched impact strength of flame-resistant PA was enhanced highly,and the elongation rate and notched impact strength of flame-resistant PP was upgraded greatly,meanwhile the apparence of products was improved.
在矿物增强阻燃复合材料中引入稀土表面改性剂对无机粉体进行活化处理,在保持阻燃性能的前提下,改善了阻燃剂及无机粉体材料与高分子材料的相容性,显著提高了阻燃PA材料的热变形温度和缺口冲击强度,明显提升了阻燃PP材料的伸长率和缺口冲击强度,产品表观状态也得到大幅度改善,阻燃复合材料的综合性能优异。
3.
The heat-resistance properties of different thermosetting resin cured systems were measured by heat distortion temperature method(HDT),differential scanning calorimetry(DSC) and dynamic mechanical analysis(DMA).
运用热变形温度(HDT)、示差扫描量热(DSC)和动态热机械分析(DMA)方法对不同热固性树脂固化体系的耐热性能进行了测试,并分析了测试结果差异与其物理机制的关系。
4) thermal deformation temperature
热变形温度
1.
Results show that thermal deformation temperature of the composites is improved evidently with incorporation of EAA and carbon black a little.
结果表明 :加入少量的乙烯 -丙烯酸共聚物 (EAA)及炭黑后 ,可使复合材料的热变形温度明显提高 ;此外 ,不同的加工工艺对复合材料的热性能也有一定的影响。
5) hot deformation temperature
热变形温度
1.
Influence of hot deformation temperature on microstructure and mechanical properties of TC18 alloy;
热变形温度对TC18钛合金显微组织和力学性能的影响
6) heat deflection temperature
热变形温度
1.
The way of heating air by using high temperature-air container was designed for the measurement of the heat deflection temperature(HDT)of polymer materials.
提出了采用加热空气介质的高温空气槽测定材料热变形温度(HDT)的方法,通过几种高分子材料在油浴中及高温空气槽中测定HDT值的比较。
补充资料：热形变温度
分子式：
分子量：
CAS号：
性质：表示塑料耐热性的一项指标。试验时，以一定升温速率2℃/分钟加热，在标准的硬质塑料试片上加一定的弯曲应力（45.1牛/厘米2即4.6公斤力/厘米2，或182.4牛/厘米2即18.6公斤力/厘米2），测定达到规定形变（0.254毫米）时的温度。表示塑料在试验条件下达到规定形变时的温度，并非表示它的使用温度上限。适用于测试热固性塑料和硬质热塑性塑料的耐热性。
分子量：
CAS号：
性质：表示塑料耐热性的一项指标。试验时，以一定升温速率2℃/分钟加热，在标准的硬质塑料试片上加一定的弯曲应力（45.1牛/厘米2即4.6公斤力/厘米2，或182.4牛/厘米2即18.6公斤力/厘米2），测定达到规定形变（0.254毫米）时的温度。表示塑料在试验条件下达到规定形变时的温度，并非表示它的使用温度上限。适用于测试热固性塑料和硬质热塑性塑料的耐热性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。