2) high iron and silicon
高硅高铁
1.
The pressure oxidative leaching of copper slag with high iron and silicon content was studied systematically.
对火法炼铅产高硅高铁含铜渣进行了氧压硫酸浸出过程研究。
3) high silicon cast iron
高硅铸铁
1.
Corrosion behavior of high silicon cast iron in several kinds of corrosion conditions;
高硅铸铁在多种环境下的腐蚀行为研究
2.
Influence of Cr on microstructure and properties of high silicon cast iron;
铬对高硅铸铁组织与性能的影响
4) high-silicon cast iron
高硅铸铁
1.
The corrosion in producing the high-concentration nitric acid from the low-concentration by magnesium nitrate process could be effectively controlled if 1Cr18Ni9Ti stainless steel, high-silicon cast iron, aluminum, C4 steel and non-metal materials were selected for the important locations of the equipment.
介绍了浓硝酸生产中的主要腐蚀现象 ,指出采用先进的自动控制的硝酸镁法浓缩稀硝酸生产工艺 ,其重要设备重点部位分别选用 1Cr18Ni9Ti不锈钢、高硅铸铁、铝材和C4钢及非金属材料 ,可取得良好的防腐蚀效
5) high-Fe and low Si
高铁贫硅
6) high silicon pig iron
高硅生铁
补充资料：高硅铁
分子式：
分子量：
CAS号：
性质：含硅约14.5%~18.0%的合金铸铁。在室温下能耐盐酸、硝酸、磷酸、乙酸等酸类的腐蚀。其耐蚀性是由于表面生成二氧化硅的薄膜，因此不耐苛性碱和氢氟酸，对还原性酸如盐酸（在沸点或较高温度）、草酸、甲酸等的耐腐蚀性差。为了提高在盐酸中的耐蚀能力，通常加入3.5%~4%的钼，称硅钼铸铁或抗氯硅铁。主要用于制作各种泵、塔、阀、反应锅、冷却器、储槽、管件和管道等设备。缺点是抗伸和抗弯强度小，脆性大，不能用于高压设备，并应避免撞击。
分子量：
CAS号：
性质：含硅约14.5%~18.0%的合金铸铁。在室温下能耐盐酸、硝酸、磷酸、乙酸等酸类的腐蚀。其耐蚀性是由于表面生成二氧化硅的薄膜，因此不耐苛性碱和氢氟酸，对还原性酸如盐酸（在沸点或较高温度）、草酸、甲酸等的耐腐蚀性差。为了提高在盐酸中的耐蚀能力，通常加入3.5%~4%的钼，称硅钼铸铁或抗氯硅铁。主要用于制作各种泵、塔、阀、反应锅、冷却器、储槽、管件和管道等设备。缺点是抗伸和抗弯强度小，脆性大，不能用于高压设备，并应避免撞击。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。