1) nylon copolycondensate
尼龙共缩聚物
2) nylon copolymer
尼龙共聚物
1.
ylon6/nylon copolymer blends were studied by DSC and WAXD.
探讨了两种尼龙共聚物对尼龙６共混改性物的热行为的影响，表明：含酰胺和酯两种基团的共聚尼龙，因其含酯基而减弱了尼龙６分子链间相互作用的结果，促进了尼龙６的结晶作用，致使冰骤冷试样观察不到冷结晶峰，仅含酰胺基团的共聚尼龙，基本上没改变尼龙６分子间的氢键相互作用，但共聚尼龙的非结晶性和无序的链结构，导致它对尼龙６结晶过程的干扰，表现为熔体结晶峰温降低和冷结晶峰温提高及峰强度（峰高）增大。
3) Nylon 1212/66 Copolymer
尼龙1212/66共聚物
4) copolyamides
尼龙1010/6共聚物
1.
Studies on the dynamic mechanical property of 1010/6 copolyamides;
尼龙1010/6共聚物动态力学性能研究
5) nylon 1010/66 copolymer
尼龙1010/66共聚物
1.
It has been studied by PLM and DSC that the thermodynamic parameters such as melting point, melting temperature range, melting heat and entropy fo nylon 1010/66 copolymers are related to their compositioms.
本文研究了尼龙1010/66共聚物的熔点、熔程、熔融热和熔融熵等热力学参数与其组成的关系,其相图中最低共熔点时尼龙1010重量比为60～70％,与理论值相近,此时熔点、熔融热和熔融熵最低,熔程最大。
6) nylon6/66 copolymer
尼龙6/66共聚物
1.
The applications of electrospun nylon6/66 copolymer nonwovens fabrics are limited because of contraction in water.
通过静电纺丝制备的尼龙6/66共聚物纳米纤维毡在水中的结构和尺寸稳定性差,这阻碍了产品的实际应用。
补充资料：尼龙共缩聚物
分子式：
分子量：
CAS号：
性质：由两种或两种以上的尼龙单体（或缩聚体）经熔融共缩聚而成的聚合物。根据所用单体（或缩聚体）种类和比例的不同，可得到从高软化点、坚硬、不易溶解到低软化点、柔软、易溶解的产物。一般来说，熔点取决于比例大的组分的摩尔分数。例如引入带环状或带侧基结构的尼龙单体，会使共绽聚尼龙有更好的醇溶解性和透明度。主要用作涂料、光敏基料、胶粘剂和塑料等。
分子量：
CAS号：
性质：由两种或两种以上的尼龙单体（或缩聚体）经熔融共缩聚而成的聚合物。根据所用单体（或缩聚体）种类和比例的不同，可得到从高软化点、坚硬、不易溶解到低软化点、柔软、易溶解的产物。一般来说，熔点取决于比例大的组分的摩尔分数。例如引入带环状或带侧基结构的尼龙单体，会使共绽聚尼龙有更好的醇溶解性和透明度。主要用作涂料、光敏基料、胶粘剂和塑料等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。