1) liquid(-phase) polycondensation
液相缩聚
2) Solution-Solid-Phase polycondensation
溶液-固相缩聚
3) solution polycondensation combined with melt polycondensation
溶液与熔融缩聚相结合
1.
In order to investigate the synthesis of Poly(butylene succinate)(PBS) screening of catalyst for polymerization reaction was used firstly,and then,biodegradable material Poly(butylenes succinate) was synthesized through melt polycondensation,solution polycondensation,and solution polycondensation combined with melt polycondensation.
为了研究PBS的合成,首先对聚合反应的催化剂进行了筛选,然后通过熔融缩聚法、溶液聚合法、溶液与熔融缩聚相结合法3种合成工艺合成了生物可降解聚酯PBS,并对合成效果进行了比较。
4) solution polycondensation
溶液缩聚
1.
Study on the direct synthesis of polylactic acid through solution polycondensation;
溶液缩聚法直接合成聚乳酸的研究
2.
Study on selection of solvents in the synthesis of polylactic acid through solution polycondensation;
溶液缩聚法合成聚乳酸中溶剂的选择研究
3.
A novel poly (ether ether ketone) derived from 4,4'-diflourodiphenylketone, bisphenol-S and 2-(6-oxide-6H-dibenz <1,2> oxa phosphorin-6-yl) -1,4-dihydroxy-phenylene was synthesized by solution polycondensation.
以9,10-二氢-9-氧杂-10-磷酰杂菲-对苯二酚(DOPO-HQ),4,4’-二氟二苯甲酮(DFK)和双酚S(DDS)为单体,通过溶液缩聚合成了含磷双酚S型聚醚醚酮。
5) Emulsion condensation polymerization
乳液缩聚
6) SSP
固相缩聚
1.
Determination the low molecular mass compound component in SSP recycle nitrogen;
固相缩聚循环氮气中低分子质量化合物组成
2.
40 kt/a PET continous SSP domestic technology;
年产4万t聚酯连续固相缩聚国产化技术
3.
Application of HOLLiAS-MACS System in SSP Plant;
HOLLiAS-MACS系统在固相缩聚装置中的应用
补充资料：液相缩聚
分子式：
分子量：
CAS号：
性质：制造缩聚物的方法之一。一般指单位在熔融状态下或在溶液中进行的缩聚反应。可用于制聚胺、聚酯等高聚物。如ω-氨基十一酸（熔点176℃）可在200-210℃经搅拌熔融缩聚成聚ω- 氨基十一酰，两种单体缩聚时，要求摩尔比相等，否则，任何一种过剩，都会使高分子的端基为过剩单体的官能团所堵塞，从而使反应中断，引起产物分子量下降。制备聚己二酰已二胺时，改用己二胺和己二酸的盐（尼龙66盐）熔融缩聚，可克服上述固难。
分子量：
CAS号：
性质：制造缩聚物的方法之一。一般指单位在熔融状态下或在溶液中进行的缩聚反应。可用于制聚胺、聚酯等高聚物。如ω-氨基十一酸（熔点176℃）可在200-210℃经搅拌熔融缩聚成聚ω- 氨基十一酰，两种单体缩聚时，要求摩尔比相等，否则，任何一种过剩，都会使高分子的端基为过剩单体的官能团所堵塞，从而使反应中断，引起产物分子量下降。制备聚己二酰已二胺时，改用己二胺和己二酸的盐（尼龙66盐）熔融缩聚，可克服上述固难。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条