1) silica modulus
硅率
2) nature sand percentage
硅砂率
1.
In the mix design,sand percentage is divided into two parts,nature sand percentage and manufactured limestone sand percentage,and then the mix design of concrete is contacted with the three ratios of cement clinker,which make the oxide constituents of concrete to be similar to those of the ce.
以混凝土材料的可循环利用为目标,提出了全新的水泥生料组分混凝土的概念,并研究了水泥生料组分混凝土的配合比设计方法——在配合比设计中引入硅砂率和钙砂率的概念,将混凝土的配合比设计与水泥生产的三率值联系起来,使混凝土的化学成分与水泥生料相同,进而在废弃后可直接作为水泥生料,无需或只需添加少量校正原料。
4) desilication efficiency
脱硅效率
5) Percentage of removal the solicit
除硅率
6) high silicate-rate
高硅酸率
1.
Here discussed is the function mechanism of calcining high silicate-rate and high strength cement clinker using steel slag and electric furnace reduced slag in place of clinker crystalseed burden and some other relevant technical problems are also dealt with in it.
论述了采用钢渣、电炉还原渣代替熟料晶种配料 ,煅烧高硅酸率高强水泥熟料的作用机理 ,对相关技术问题进行了探讨。
补充资料：硅率
分子式：
CAS号：
性质：又称硅率。用SM或n表示。硅酸盐水泥生产中控制生、熟料中酸性氧化物之间比例的参数之一，表示生料或熟料中氧化硅含量与氧化铝、氧化铁之和的质量百分数之比，其计算式为：。通常硅酸盐水泥熟料的硅率在1.7～2.7之间，白水泥的硅率在4.0左右。硅率也表示了熟料中硅酸盐矿物与熔剂矿物的比例。硅率过高，则煅烧时熟料中液相量少，要求煅烧温度高，硅率太低，熟料中液相量过多，煅烧时易出现结大块、结炉瘤、结圈等现象，影响窑的操作。
CAS号：
性质：又称硅率。用SM或n表示。硅酸盐水泥生产中控制生、熟料中酸性氧化物之间比例的参数之一，表示生料或熟料中氧化硅含量与氧化铝、氧化铁之和的质量百分数之比，其计算式为：。通常硅酸盐水泥熟料的硅率在1.7～2.7之间，白水泥的硅率在4.0左右。硅率也表示了熟料中硅酸盐矿物与熔剂矿物的比例。硅率过高，则煅烧时熟料中液相量少，要求煅烧温度高，硅率太低，熟料中液相量过多，煅烧时易出现结大块、结炉瘤、结圈等现象，影响窑的操作。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条