1) aluminium silicate fiber reinforcement
硅酸铝纤维增强体
2) high-purity aluminium silicate fiber
高纯硅酸铝纤维增强体
3) strength / aluminium silicate fibers
强度/硅酸铝纤维
5) Al-silicate fibre reinforced MMC
硅酸铝短纤维强化MMC
6) aluminum silicate fibers
硅酸铝纤维
1.
Al2O3-SiO2/AZ91D magnesium matrix composites with compacted structure were prepared with aluminum silicate fibers and AZ91D magnesium alloy by squeeze casting method.
采用硅酸铝纤维和镁合金制备出结构紧密的Al2O3-SiO2/AZ91D镁基复合材料。
2.
Specific to difficult for aluminum silicate fibers into paper and intensity of the paper is not high,Through a series of experiments researched on carboxyl methyl cellulose (CMC),modified polyvi- nyl alcohol (PVA),cationic starch are commonly used on adhesive,which effected on aluminum silicon fibers into paper,performance of strength.
针对硅酸铝纤维难成纸且成纸强度不高的问题,本文通过一系列实验研究了羧甲基纤维素(CMC)、改性聚乙烯醇(PVA)、阳离子淀粉(CS)三种常用胶粘剂对硅酸铝纤维成纸、增强性能的影响。
补充资料：硅酸铝纤维增强体
分子式：
CAS号：
性质：主要成分为氧化铝、二氧化硅和少量添加氧化硼或氧化锆的纤维。有晶质纤维和非晶质纤维两种。纤维直径一般为9μn)，密度3.2g/cm3，拉伸强度2.6GPa，模量260GPa，可耐1300℃。采用干法纺丝，再600℃裂解法制取。用于增强铅基复合材料，制造高性能发动机部件。
CAS号：
性质：主要成分为氧化铝、二氧化硅和少量添加氧化硼或氧化锆的纤维。有晶质纤维和非晶质纤维两种。纤维直径一般为9μn)，密度3.2g/cm3，拉伸强度2.6GPa，模量260GPa，可耐1300℃。采用干法纺丝，再600℃裂解法制取。用于增强铅基复合材料，制造高性能发动机部件。