1) norbornylene bisphenol polycarbonate
亚降冰片基双酚聚碳酸酯
2) norbornylene bisphenol-thiobisphenol copolycarbonate
亚降冰片基双酚-硫代二苯酚共聚碳酸酯
3) norbornylene bisphenol-thiobisphenol copolycarbonate
亚降冰片基双酚-二羟基苯基硫共聚碳酸酯
4) bisphenol-A pOlycarbonate
双酚A型聚碳酸酯
1.
Bisphenol-A polycarbonate/dioctyl phthalate blend samples crystallized at a hydrostatic pressure were investigated by WAXD,DSC and SEM measurements.
双酚A型聚碳酸酯(BAPC)作为一种本体结晶速率极为缓慢的高聚物是研究高分子结晶行为[5~11]的理想对象。
5) bisphenol-A polycarbonate
双酚A聚碳酸酯
1.
Advances in new methods for synthesis of bisphenol-A polycarbonate;
双酚A聚碳酸酯合成新方法的研究进展
2.
Acetone,tetrahydrofuran,butyl acetate and carbon tetrachloride in liquid state were used to induce the crystallization of bisphenol-A polycarbonate (BAPC) film.
采用丙酮、四氢呋喃、乙酸丁酯和四氯化碳等有机溶剂对双酚A聚碳酸酯(BAPC)进行诱导结晶。
3.
5 kPa) crystallization behavior of bisphenol-A polycarbonate (BAPC) at 298 K was studied and compared.
5kPa蒸气压的气相丙酮,对双酚A聚碳酸酯(BAPC)的液相或气相诱导结晶行为进行研究。
6) bisphenol A polycarbonate
双酚A型聚碳酸酯
1.
In the process of internal friction measurement of polyamide 1010 (PAlOlO)and its blends with bisphenol A polycarbonate (PC) ,it was found that the relaxation temperatures bore close relation to the starting temperature for measurement.
本工作对尼龙1010(PA1010)及其与双酚A型聚碳酸酯(PC)的共混物进行了内耗测量,发现它们的内耗峰温与测量起始温度有密切联系。
补充资料：亚降冰片基双酚聚碳酸酯
分子式：
CAS号：
性质：分子链含亚降冰片基双酚型碳酸酯结构的聚合物。有不同结构降冰片基双酚的均聚物和共聚物之分,性能有所不同。但总的特点是耐温性好，强度高。玻璃化转变温度224℃,热变形温度233℃；拉伸强度38.61MPa，拉伸模量1585.8MPa，体积电阻率1.0×1018Ω·cm，介电常数3.04～3.09。由亚降冰片基双酚与光气反应制得。可注塑成所需制品。其薄膜可用作驻极体的电容器传声器隔膜，使用寿命10年以上。
CAS号：
性质：分子链含亚降冰片基双酚型碳酸酯结构的聚合物。有不同结构降冰片基双酚的均聚物和共聚物之分,性能有所不同。但总的特点是耐温性好，强度高。玻璃化转变温度224℃,热变形温度233℃；拉伸强度38.61MPa，拉伸模量1585.8MPa，体积电阻率1.0×1018Ω·cm，介电常数3.04～3.09。由亚降冰片基双酚与光气反应制得。可注塑成所需制品。其薄膜可用作驻极体的电容器传声器隔膜，使用寿命10年以上。