1) EVA hollow fiber membrane
乙烯-醋酸乙烯酯共聚物中空纤维膜
2) polyethylene/ethylene-vinyl acetate copolymer film
聚乙烯/乙烯-醋酸乙烯酯共聚物薄膜
3) ethylene-vinyl acetate copolymer fiber
乙烯-醋酸乙烯共聚纤维
4) ethylene-vinyl acetate copolymer fiber
乙烯醋酸乙烯共聚纤维
5) ethylene vinyl-acetate copolymer
乙烯/醋酸乙烯酯共聚物
1.
The photocrosslinking of ethylene vinyl-acetate copolymer (EVA) containing phosphorus- nitrogen halogen-free flame retardant (EM82) was studied,It found that the EVA/EM82 samples with a thickness of 1.
对磷氮类阻燃剂(EM82)无卤阻燃乙烯/醋酸乙烯酯共聚物(EVA)复合材料进行了紫外光交联研究。
6) EVA
乙烯-醋酸乙烯酯共聚物
1.
Ammonium polyphosphate(APP) and expandable graphite(EG) have been used to improve flame retardancy of poly(ethylene-co-vinyl acetate)(EVA).
对聚磷酸铵(APP)和膨胀石墨(EG)协同阻燃乙烯-醋酸乙烯酯共聚物(EVA)及其阻燃机理进行了研究。
2.
Flame retardation of EVA copolymer using melamine phosphate(MP) and pentaerythritol(PER) as intumescent flame retardants(IFR) was investigated.
研究了三聚氰胺磷酸盐(M P)和季戊四醇(PER)作为膨胀型阻燃剂(IFR)在乙烯-醋酸乙烯酯共聚物(EVA)中的阻燃作用。
3.
Blend of ethylene-vinyl acetate copolymer(EVA),ethylene-propylene-diene terpolymer rubber(EPDM) and chlorinated polyethylene(CPE) was cross-linked with dicumyl peroxide(DCP) and blown simultaneously with azodicarbonamide(AC) by injecting,cross-linking and blowing process.
乙烯-醋酸乙烯酯共聚物(EVA)、三元乙丙橡胶(EPDM)和氯化聚乙烯(CPE)经熔融共混和注射,用过氧化二异丙苯(DCP)引发交联,同时经偶氮二碳酰胺(AC)发泡成交联发泡材料,其力学性能与配方、交联发泡温度和时间有关,较适宜的温度为440 K~450 K,最佳的温度和时间分别为448 K和360s。
补充资料：乙烯-醋酸乙烯酯共聚物中空纤维膜
分子式：
CAS号：
性质：具有超滤、透析和血浆分离等功能的EVA中空纤维。纤维内径200μm，膜厚50μm，膜微孔孔径0.01～0.03μm。将乙烯-醋酸乙烯共聚物溶于适当溶剂中并通过中空喷丝板进行干-湿纺而得。用于血浆分离、血浆成分分离和人工肾等。
CAS号：
性质：具有超滤、透析和血浆分离等功能的EVA中空纤维。纤维内径200μm，膜厚50μm，膜微孔孔径0.01～0.03μm。将乙烯-醋酸乙烯共聚物溶于适当溶剂中并通过中空喷丝板进行干-湿纺而得。用于血浆分离、血浆成分分离和人工肾等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条