1) ethylhydrosilicone fluid
乙基含氢硅油
2) Methyl hydrogen silicone fluid
甲基含氢硅油
1.
The influence of titanium isopropoxide on the anti-contamination agent curing speed in benzinum solvent , and the influence of methyl hydrogen silicone fluid and titanium isopropoxide content on the proofing functio.
文中还讨论了以石油醚为溶剂的钛酸四异丙酯对防污剂固化速度的影响以及甲基含氢硅油和钛酸四异丙酯的含量对防污性的影响。
2.
This paper also studied the proofing function influence produced by methyl hydrogen silicone fluid content and tita.
讨论了以石油醚为溶剂钛酸四异丙酯对防污剂固化速度的影响、甲基含氢硅油和钛酸四异丙酯的含量对防污性的影响。
3) poly(methylhydrosiloxane)
含氢硅油
1.
Synthesis and characterization of poly(methylhydrosiloxane)with n-butyl methacrylate;
甲基丙烯酸正丁酯-含氢硅油的合成与表征
2.
01%) of the raw material weight,a series of water-based fluorosilicone were synthesized by using poly(methylhydrosiloxane),organoflurine,allyl polyoxyethylene polyoxypropylene ether,and silicane coupling agent.
01%以及无溶剂的条件下,采用硅氢加成法将烯丙基聚氧乙烯聚氧丙烯醚、含氟单体及硅烷偶联剂与低含氢硅油进行接枝共聚,成功地制备了一系列有机氟硅聚合物。
3.
Without solvent, a series of water-based fluorosilicone polymers were synthesized from allyl polyoxyethylene polyoxypropylene ether, organic fluoride and poly(methylhydrosiloxane) via hydrosilyla- tion, and the aqueous dispersions of the polymers were obtained by the way of emulsification.
在无溶剂的条件下,通过硅氢加成法将烯丙基聚氧乙烯聚氧丙烯醚,氟化丙烯酸烷基酯接枝共聚到甲基含氢硅油侧链,成功地合成了一系列有机氟硅聚合物。
4) hydrogen containing silicone fluid
含氢硅油
1.
Polyether modified polysiloxane was synthesized by the hydrosilation reaction of hydrogen containing silicone fluid (PHDS)and allyl polyether(APE), using chloroplatinic acid as the catalyst.
以氯铂酸为催化剂 ,利用含氢硅油 (PHDS)与烯丙基聚醚 (APE)的硅氢加成反应 ,合成出聚醚改性硅油 ;然后用乙醇胺进行胺化反应 ,制成纸张用氨基改性聚醚硅油柔软剂。
2.
s:Mass fraction of active hydrogen in hydrogen containing silicone fluid was calculated bases on integrate area of testable hydrogen proton peak by 1 H NMR taking benzene as classic inner standard matter.
以苯为内标物 ,采用核磁共振 ( 1HNMR)法 ,根据可测试的氢质子峰的积分面积 ,计算出含氢硅油中活性氢的质量分数。
5) h-silicone oil
含氢硅油
1.
The wool fabric was treated by amino silicone oil,h-silicone oil combine with low temperature plasma(LTP) to improve the anti-felting property.
经氨基硅油处理后等离子体照射,再用含氢硅油处理后等离子体照射工艺处理的羊毛织物,毡缩率降低到7。
2.
The wool fabric was treated by amino silicone oil,h-silicone oil combine with low temperature plasma(LTP)to improve the anti-felting property.
经氨基硅油处理后等离子照射,再用含氢硅油处理后等离子照射工艺处理的羊毛织物毡缩率降低到7。
6) hydrogen-containing silicone oil
含氢硅油
1.
The effects on the condition of hydrosilylation and the conversion of hydrogen-containing silicone oil were studied.
以不饱和的聚醚和环氧氯丙烷为原料,合成出环氧不饱和聚醚;再与低含氢硅油进行硅氢加成反应,合成出环氧聚醚改性聚甲基硅氧烷;接着用二甲胺对环氧基开环,得到二甲胺聚醚改性有机硅表面活性剂。
2.
The hydrogen-containing silicone oil with different content of active hydrogen was synthesized by taking high hydrogen-containing silicone oil and D_4 as material,macropore cation resin as catalyst.
以八甲基环四硅氧烷(D4)、乙烯基双封头和乙烯基环体为原料,四甲基氢氧化铵为催化剂,合成出不同摩尔质量和乙烯基含量的乙烯基硅油;以高含氢硅油、D4为原料,大孔阳离子树脂为催化剂,合成出活性氢质量分数不同的含氢硅油。
补充资料：乙基含氢硅油
分子式：
CAS号：
性质：无色透明油状物，黏度一般为1～5×10-2pa·s。相对密度0.98～1.10。折射率1.390～1.420，氢含量0.8％～1.2％。在醇碱作用下，Si—H键断裂，放出氢气。在铂催化剂作用下，Si—H键可与链烯烃进行加成反应。在有机金属化合物存在下，可交联成膜，具有优良的憎水防潮性能。可由乙基二氯硅烷和三乙基氯硅烷共水解缩合来制取。广泛用于纺织、皮革、陶瓷、玻璃和建材的防水处理，也可用作橡胶制品的脱模剂和织机润滑油添加剂。
CAS号：
性质：无色透明油状物，黏度一般为1～5×10-2pa·s。相对密度0.98～1.10。折射率1.390～1.420，氢含量0.8％～1.2％。在醇碱作用下，Si—H键断裂，放出氢气。在铂催化剂作用下，Si—H键可与链烯烃进行加成反应。在有机金属化合物存在下，可交联成膜，具有优良的憎水防潮性能。可由乙基二氯硅烷和三乙基氯硅烷共水解缩合来制取。广泛用于纺织、皮革、陶瓷、玻璃和建材的防水处理，也可用作橡胶制品的脱模剂和织机润滑油添加剂。