1) brominated bisphenol A epoxy resin
溴代双酚A环氧树脂
2) tetrabromo-bisphenol-A epoxy resin
四溴双酚A环氧树脂
1.
By means of fourier transform infrared(FTIR), the curing kinetics of bisphenol-S epoxy resin/DDS and tetrabromo-bisphenol-A epoxy resin/DDS at constant temperature were studied, and the apparent activation energy was obtained.
用傅里叶红外光谱 (FTIR)法研究了双酚S环氧树脂和四溴双酚A环氧树脂分别与二胺基二苯砜在恒温条件下的固化反应动力学 ,得出了各反应的表观活化能。
3) brominated epoxy resin
溴代环氧树脂
4) Bromine-containing naphthol formaldehyde epoxy resin
含溴萘酚酚醛环氧树脂
5) bisphenol A epoxy resin
双酚A型环氧树脂
1.
The effects of curing temperature and the content of on the curing speed of PSN-1 polysilazane/bisphenol A epoxy resin curing system were discussed.
研究了聚硅氮烷(PSN-1)/双酚A型环氧树脂固化体系的固化温度、PSN-1用量对固化速度的影响;并利用热重分析(TGA)研究了PSN-1用量对固化树脂高温残余质量分数的影响,对固化机理进行了初步探讨。
6) bisphenol A epoxy resin
双酚A环氧树脂
1.
Describe the production prenciple,raw material and process of bisphenol A epoxy resin.
描述了双酚A环氧树脂生产的反应机理 ,原材料 ,主要建筑用胶的性能和特点及质量参
补充资料：溴代双酚A环氧树脂
分子式：
CAS号：
性质：又称溴代双酚A环氧树脂。俗称EX型环氧树脂。含溴元素的双酚A缩水甘油醚。以四溴双酚A环氧树脂或四溴双酚A二缩水甘油醚为主。且有溴含量48％～50％高溴化树脂(HBR)、四溴双酚与双酚A共聚而成的溴含量20％～24％的低溴化树脂(LBR)两种。HBR环氧当量350～602，软化温度71～101℃。固化物热变形温度147～153℃；拉伸强度(MPa)34.3～47.1，弯曲强度(MPa)130.4～140.3，悬臂梁(Izod)冲击强度(kJ/m2)1.57～1.68。化学稳定性和机械强度与双酚A环氧树脂相近，且与之相容性好。由四溴双酚A与环氧氯丙烷反应、或四溴双酚A与双酚A环氧树脂加聚而成。可用作阻燃灌封料、层合板、模塑料、胶黏剂、涂料；阻燃剂等。用于建筑、航空、电子工业等方面。 6-溴(代)菲啶 6-bromophenanthridine 熔点125～126℃。用菲啶酮与三溴化磷反应制得。将菲啶用N-溴(代)琥珀酰亚胺溴化时，得到2-溴代菲啶(熔点162～163℃)。用溴与硫酸银及硫酸将菲啶溴化时，得到混合物。用作有机合成试剂。
CAS号：
性质：又称溴代双酚A环氧树脂。俗称EX型环氧树脂。含溴元素的双酚A缩水甘油醚。以四溴双酚A环氧树脂或四溴双酚A二缩水甘油醚为主。且有溴含量48％～50％高溴化树脂(HBR)、四溴双酚与双酚A共聚而成的溴含量20％～24％的低溴化树脂(LBR)两种。HBR环氧当量350～602，软化温度71～101℃。固化物热变形温度147～153℃；拉伸强度(MPa)34.3～47.1，弯曲强度(MPa)130.4～140.3，悬臂梁(Izod)冲击强度(kJ/m2)1.57～1.68。化学稳定性和机械强度与双酚A环氧树脂相近，且与之相容性好。由四溴双酚A与环氧氯丙烷反应、或四溴双酚A与双酚A环氧树脂加聚而成。可用作阻燃灌封料、层合板、模塑料、胶黏剂、涂料；阻燃剂等。用于建筑、航空、电子工业等方面。 6-溴(代)菲啶 6-bromophenanthridine 熔点125～126℃。用菲啶酮与三溴化磷反应制得。将菲啶用N-溴(代)琥珀酰亚胺溴化时，得到2-溴代菲啶(熔点162～163℃)。用溴与硫酸银及硫酸将菲啶溴化时，得到混合物。用作有机合成试剂。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。