1) alumina fiber
多晶氧化铝纤维
2) Alumina fiber
氧化铝纤维
1.
Influences of burning temperatures on alumina fiber reinforced andalusite composites;
烧成温度对氧化铝纤维/红柱石复合材料性能的影响
2.
The results indicate that the alumina fibers is uniform in distribution and can serve as the sites for heterogeneous nucleation of silicon phase,and that the interfaces between the fibers and the aluminum alloy matrix have a great effect on the mechanical properties of the composites.
结果表明 ,在复合材料中纤维分布均匀 ,氧化铝纤维可作为硅相非自发形核的衬底 ;氧化铝纤维与铝合金基体之间的界面对材料性能影响很大。
3.
In this paper,the features of the new generation of continuous high-strength alumina fiber rein- forced aluminum composites,and their value and potential for applications are discussed in the respects of its fabrica- tion,performanee and application.
从制备、性能和应用几个方面概述了近几年新兴的连续高强氧化铝纤维增强铝基复合材料的特点,以及该类复合材料所具有的良好应用价值和应用前景。
3) Al2O3 fiber
氧化铝纤维
1.
(Al2O3f+Cf)composites were fabricated by squeezing casting, the appearance of carbon fiber and Al2O3 fiber before-and-after pretreatment were investigated by scanning electron microscope.
采用挤压铸造法制备氧化铝纤维和碳纤维混杂增强ZL109复合材料,SEM观察预处理前后的氧化铝纤维、碳纤维的形貌,金相显微镜观察纤维在复合材料中的分布。
6) polycrystalline zirconium dioxide fibre
多晶二氧化锆纤维
补充资料：多晶氧化铝纤维
分子式：
CAS号：
性质：又称多晶氧化铝纤维。制法不同其Al2O3的结晶态和含量各异。直径10～20μm。密度2.7～4.2g/cm3。强度1.4～2.45GPa。模量190～385GPa。最高使用温度为1100～1400℃。制法：(1)前驱体法，将聚铝噁烷与硅酸酯载体溶于有机溶剂中干纺，在1000℃空气中烧成，得到含SiO2的γ-Al2O3纤维；更换原料和载体可得α-Al2O3-ZrO2纤维；(2)淤浆法，将α-Al2O3粉、Al(OH)2Cl·2H2O及少量MgCl2·6H2O所组成的淤浆干纺，在1000～1500℃烧成而得α-Al2O3纤维；(3)胶体法，在含HCOO-和CH3COO-离子的Al2O3溶胶中加入硅溶胶和硼酸，纺丝后烧成而得(9Al2O3·2B2O3+无定形SiO2)纤维。用作结构和功能复合材料增强剂，如电磁波屏蔽材料等。
CAS号：
性质：又称多晶氧化铝纤维。制法不同其Al2O3的结晶态和含量各异。直径10～20μm。密度2.7～4.2g/cm3。强度1.4～2.45GPa。模量190～385GPa。最高使用温度为1100～1400℃。制法：(1)前驱体法，将聚铝噁烷与硅酸酯载体溶于有机溶剂中干纺，在1000℃空气中烧成，得到含SiO2的γ-Al2O3纤维；更换原料和载体可得α-Al2O3-ZrO2纤维；(2)淤浆法，将α-Al2O3粉、Al(OH)2Cl·2H2O及少量MgCl2·6H2O所组成的淤浆干纺，在1000～1500℃烧成而得α-Al2O3纤维；(3)胶体法，在含HCOO-和CH3COO-离子的Al2O3溶胶中加入硅溶胶和硼酸，纺丝后烧成而得(9Al2O3·2B2O3+无定形SiO2)纤维。用作结构和功能复合材料增强剂，如电磁波屏蔽材料等。