1) compressive strength of cellular plastics
微孔塑料压缩强度
2) microcellular plastic
微孔塑料
1.
Application of supercritical CO_2 in preparation of microcellular plastics in continuous extrusion;
超临界CO_2在连续挤出微孔塑料中的应用
2.
The conception, foaming principle, phylogeny and four preparation method including thermally induced phase separation, monomer polymerization reaction, gas supersaturation and precipitation with a compressed fluid antisolvent of microcellular plastic were summarized.
主要介绍微孔塑料的概念、发泡原理、发展简史和热诱导相分离法、单体聚合反应法、超饱和气体法、压缩流体反溶剂沉淀法四种常用的制备技术,并详细综述了国外在微孔复合材料、微孔生物医学材料、微孔橡胶材料和其它方面的最新发展动态及应用。
3.
The application of supercritical CO_2 in extrusion process was discussed respectively according to de- crease the polymer melt viscosity and as a foam agent for prepare the microcellular plastic.
本文阐述超临界CO_2在挤出过程中的应用——降低聚合物的黏度和作为发泡剂制备微孔塑料,综述了其国内外的研究现状。
3) microcellular plastics
微孔塑料
1.
Study of Moulding Process of Microcellular Plastics;
微孔塑料成型加工的研究
2.
Study of Supercritical Fluid in Extrusion of Microcellular Plastics;
超临界流体辅助挤出微孔塑料的研究
3.
Study on Effects of Vibration on Cell Structure of PS and PVC Microcellular Plastics;
振动作用对PS和PVC微孔塑料泡孔结构影响的研究
4) micro porous PE pipe
微孔塑料管
5) supermicrocellular plastics
超微孔塑料
1.
Compared with traditional foaming plastics, supermicrocellular plastics has many excellent characters.
超微孔塑料是一种新型的高分子材料 ,与传统的泡沫塑料相比具有很多优异的性能。
6) compression strength
压缩强度
1.
Preparation of high compression strength polyacrylate/polysiloxane interpenetrating network hydrogel;
高压缩强度聚丙烯酸盐/聚硅氧烷互穿网络水凝胶的制备
2.
The compression strength of pitch derived car.
将高温煤沥青和浸渍剂沥青在不同压力下炭化,在2500℃下对所得沥青炭进行石墨化处理;测试了所得沥青炭的体积密度、开孔率;利用扫描电子显微镜(SEM)观察了所得沥青炭的显微结构;利用XRD检测了所得沥青炭石墨化处理后的石墨化度;测试了所得沥青炭的压缩强度。
3.
The structure,thermal stability,especially the effects of isothermal annealing on the microhardness and compression strength of this bulk metallic glass were investigated by X-ray diffraction,differential scanning calorimetry,microhardness and compression tests.
采用X射线衍射(XRD)、示差扫描量热(DSC)、显微硬度及压缩试验等方法研究了非晶合金的结构、热稳定性,特别是等温热处理对其显微硬度与压缩强度的影响。
补充资料：微孔塑料压缩强度
分子式：
CAS号：
性质：微孔塑料相对变形小于10％时所达到的最大压缩力与试样原始横截面积之比。如果最大应力值所对应的相对变形低于10％，则记作“压缩强度”。这时要计算相对变形为10％的压缩应力，则称该值为“相对变形为10％的压缩应力”。对于微孔塑料专门规定这一力学量是因为该材料不同于一般均质材料的缘故。