2) flex stiff-ness
耐屈挠疲劳
3) flex fatigue property
耐屈挠疲劳性能
1.
The results showed that when the CTPI was added to CR/TPI blend,the scorch time and optimum curing time of CR/TPI blend reduced,the compatibility between TPI and CR increased,and then the dispersity of carbon black and the flex fatigue property were improved.
结果表明,在CR/TPI并用胶中加入CTPI可缩短胶料的焦烧时间和正硫化时间,改善TPI与CR的相容性,从而改善胶料中炭黑的分散性,显著提高胶料的耐屈挠疲劳性能。
4) flex fatigue test
屈挠疲劳试验
5) flexing fatigue resistance
耐屈挠疲劳破坏性能
1.
The network of fillers was reinforced,the mechanical properties as well as the flexing fatigue resistance were improved,the wearing resistance was improved by 15%-30%,and the rolling resistance was reduced.
结果表明,黏土的加入不会对胶料的硫化特性产生太大影响;少量黏土的加入增强了混炼胶的填料网络作用,改善了炭黑/NR硫化胶的物理机械性能,耐磨性能提高了15%~30%,降低了滚动阻力,提高了耐屈挠疲劳破坏性能,当黏土填充量为4份时,复合材料的综合性能最优。
6) fatigue yield limit
疲劳屈服点
补充资料：屈挠疲劳
分子式：
CAS号：
性质：又称屈挠疲劳。材料在交变弯曲应力作用下发生损伤乃至断裂的过程。在疲劳初期，内部结构将发生改变，接着出现疲劳裂纹的成核和扩展，当疲劳裂纹失稳扩展时就导致疲劳断裂。在作弯曲疲劳试验时，按控制变量，可分为应力疲劳和应变疲劳两类。应力疲劳时，应力幅值恒定在一较低值，加载的频率高，断裂周次也高；应变疲劳时，应力幅值恒定在较高值，加载频率低，断裂周次也低。弯曲疲劳是工程实际中经常会发生的问题，弯曲疲劳试验也是材料疲劳试验方法中比较成熟的一种方法。
CAS号：
性质：又称屈挠疲劳。材料在交变弯曲应力作用下发生损伤乃至断裂的过程。在疲劳初期，内部结构将发生改变，接着出现疲劳裂纹的成核和扩展，当疲劳裂纹失稳扩展时就导致疲劳断裂。在作弯曲疲劳试验时，按控制变量，可分为应力疲劳和应变疲劳两类。应力疲劳时，应力幅值恒定在一较低值，加载的频率高，断裂周次也高；应变疲劳时，应力幅值恒定在较高值，加载频率低，断裂周次也低。弯曲疲劳是工程实际中经常会发生的问题，弯曲疲劳试验也是材料疲劳试验方法中比较成熟的一种方法。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条