2) glass fiber reinforced poly (phenylene sulfide)
玻璃纤维增强聚苯硫醚
3) polyphenylene sulfide/carbon fiber
聚苯硫醚/碳纤维
4) carbon fibers reinforced polyetheretherketone(CFR/PEEK)
碳纤维增强聚醚醚酮
1.
The surface tension of comparison of titanium alloy,polyetheretherketone(PEEK),and carbon fibers reinforced polyetheretherketone(CFR/PEEK)
钛合金、聚醚醚酮(PEEK)和碳纤维增强聚醚醚酮(CFR/PEEK)~*表面张力的比较
5) CF/PPEK
碳纤维增强杂萘联苯聚醚酮
1.
In this paper pre-impregnated hot compression molding process of the CF/PPEK and CF/PPES unidirectional compound plates were studied and mechanical properties of prepared unidirectional composites were discussed by experiment.
本文研究了碳纤维增强杂萘联苯聚醚酮(CF/PPEK)和碳纤维增强杂萘联苯聚醚砜(CF/PPES)2 种 复合材料单向板的预浸热压成型工艺,对制备的单向板进行了力学性能试验研究,并利用 X 射线光电子能 谱(XPS)和扫描电子显微镜(SEM)对这两种复合材料的界面状态和结构进行了分析。
6) CF/PPES
碳纤维增强杂萘联苯聚醚砜
1.
In this paper pre-impregnated hot compression molding process of the CF/PPEK and CF/PPES unidirectional compound plates were studied and mechanical properties of prepared unidirectional composites were discussed by experiment.
本文研究了碳纤维增强杂萘联苯聚醚酮(CF/PPEK)和碳纤维增强杂萘联苯聚醚砜(CF/PPES)2 种 复合材料单向板的预浸热压成型工艺,对制备的单向板进行了力学性能试验研究,并利用 X 射线光电子能 谱(XPS)和扫描电子显微镜(SEM)对这两种复合材料的界面状态和结构进行了分析。
补充资料：碳纤维增强聚苯硫醚
分子式：
CAS号：
性质：含有碳纤维组分，某些力学性能较原树脂有较大提高的聚苯硫醚复合物及其制品。含30％碳纤维的增强聚苯硫醚，相对密度1.42；吸水性0.02％；拉伸强度172.3MPa，拉伸模量25.5GPa，弯曲强度213.7MPa，弯曲模量17.2GPa，压缩强度179.3MPa，缺口冲击强度64J/m，无缺口冲击强度213J/m；热变形温度(1.82MPa)260℃。由碳纤维与聚苯硫醚在一定条件下均匀混合制得。可用作汽车、电子电器和航天工业用零部件。也可用作电磁屏蔽和防静电制品。
CAS号：
性质：含有碳纤维组分，某些力学性能较原树脂有较大提高的聚苯硫醚复合物及其制品。含30％碳纤维的增强聚苯硫醚，相对密度1.42；吸水性0.02％；拉伸强度172.3MPa，拉伸模量25.5GPa，弯曲强度213.7MPa，弯曲模量17.2GPa，压缩强度179.3MPa，缺口冲击强度64J/m，无缺口冲击强度213J/m；热变形温度(1.82MPa)260℃。由碳纤维与聚苯硫醚在一定条件下均匀混合制得。可用作汽车、电子电器和航天工业用零部件。也可用作电磁屏蔽和防静电制品。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。