1) silicon carbide whisker reinforcement
碳化硅晶须增强体
2) silicon carbide platelet reinforcement α-SiC
碳化硅晶板增强体
3) silicon carbide whisker reinforced Al-matrix composite
碳化硅晶须增强铝基复合材料
4) sic-cvystall increasingly-malleable ceramics
碳化硅晶须增韧陶瓷
5) silicon carbide whisker
碳化硅晶须
1.
The key process parameters for the double-heating synthesis of silicon carbide whiskers with carbon black and SiO2 powders as raw materials are studied.
双重加热法是低成本、大批量合成碳化硅晶须的新技术,合成温度低、合成时间短、生成率高。
2.
The heat conductive silicone rubber with vinyl endblocked polymethylsiloxane as basic gum and silicone nitride(Si_3N_4) of different particle sizes and silicon carbide whisker as fillers was prepared.
以甲基乙烯基硅橡胶为基胶,选用不同粒径氮化硅粒子和碳化硅晶须为填料制备了导热硅橡胶。
3.
The silicon carbide whiskers and platelets are ideal reinforcements of compound materials of ceramic,metal and resin.
碳化硅晶须和晶片都是陶瓷基、金属基、树脂基复合材料的理想增强体,与碳化硅晶须相比,有关碳化硅晶片制备与应用的报道相对较少。
6) silicon carbide whiskers
碳化硅晶须
1.
All kinds of approach and the mechanism to synthesize silicon carbide whiskers are commented on , and the progress of silicon carbide whiskers at home and abroad is also reviewed.
比较详细地介绍了当前国内外碳化硅晶须的生长机理与制备方法，简要评述了对碳化 硅晶须研究的进展状况。
2.
Carbon nanotubes (CNTs) and silicon carbide whiskers (SiCw) are promising reinforcement materials for manufacturing metal or ceramic based composites.
在制备复合材料中,碳纳米管和碳化硅晶须易受到空气和基体材料侵蚀而失效。
补充资料：碳化硅晶须增强体
分子式：
CAS号：
性质：一种黄绿色或灰绿色的短纤维。直径0.2～1.5μm，粗晶须可达3～5/μm，长度为几十至数百微米，最长者达500μm。密度3.2g/cm3。熔点2690℃，比强度6.4cm(接近理论计算值6.9cm)。采用化学气相沉积法制取。用作氧化铝陶瓷和氮化硅陶瓷增强体制造切削刀具。
CAS号：
性质：一种黄绿色或灰绿色的短纤维。直径0.2～1.5μm，粗晶须可达3～5/μm，长度为几十至数百微米，最长者达500μm。密度3.2g/cm3。熔点2690℃，比强度6.4cm(接近理论计算值6.9cm)。采用化学气相沉积法制取。用作氧化铝陶瓷和氮化硅陶瓷增强体制造切削刀具。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条